Haynes 282® Nickel Alloy Plate, Solution Annealed and Age-Hardened, after long term high temperature exposure

Category Metal , Nonferrous Metal , Nickel Alloy
Manufacturer Haynes International, Inc.
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Haynes 282® Nickel Alloy Plate, Solution Annealed and Age-Hardened, after long term high temperature exposure.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Excellent High Temperature Strength HAYNES® 282® alloy is a wrought, gamma-prime strengthened superalloy developed for high temperature structural applications, especially those in aero and land-based gas turbine engines. It possesses a unique combination of creep strength, thermal stability, weldability, and fabricability not found in currently available commercial alloys. The alloy has excellent creep strength in the temperature range of 1200 to 1700°F (649 to 927°C), surpassing that of Waspaloy alloy, and approaching that of R-41 alloy. Easily Fabricated: This high level of creep strength in HAYNES 282 alloy has been attained at a relatively low volume fraction of the strengthening gamma-prime phase, resulting in outstanding resistance to strain-age cracking (normally a problem with superalloys in this creep strength range). Additionally, slow gamma-prime precipitation kinetics allow for the alloy to have excellent ductility in the as-annealed condition. Consequently, HAYNES 282 alloy exhibits superior weldability and fabricability. Product Forms: HAYNES 282 alloy is designed for use in the form of plate, sheet, strip, foil, billet, bar, wire welding products, pipe, and tubing. Heat Treatment: HAYNES 282 alloy is provided in the solution-annealed condition, in which it is readily formable. The typical solution annealing temperature is in the range of 2050 to 2100°F (1121 to 1149°C). After component fabrication, a two-step age hardening treatment is required to put the alloy into the high-strength condition. The treatment includes 1850°F (1010°C) / 2 hours / AC (air cool) + 1450°F (788°C) / 8 hours / AC. Applications: Suitable for critical gas turbine applications, such as sheet fabrications, seamless and flash butt-welded rings, and cases found in compressor, combustor, and turbine sections. In augmented aircraft gas turbines, it is useful for exhaust and nozzle components. In land-based gas turbines, HAYNES 282 alloy is a good candidate for transition sections and other hot-gas-path components. Machining: HAYNES 282 alloy has similar machining characteristics to other nickel alloys used at high temperatures. Rough machining should be carried out prior to age-hardening, using the following guidelines. Final machining or finish grinding may be done after age-hardening.Data provided by the manufacturer, Haynes International, Inc.
Physical Properties Metric English Comments
Density 8.27 g/cc
0.299 lb/in³
Solution Annealed
8.29 g/cc
0.299 lb/in³
Age-hardened
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 1152 MPa
167100 psi
Room temp test prior to thermal exposure
978 MPa

@Treatment Temp. 871 °C,
Time 5.76e+7 sec
142000 psi

@Treatment Temp. 1600 °F,
Time 16000 hour
Room temp test after thermal exposure
1006 MPa

@Treatment Temp. 871 °C,
Time 2.88e+7 sec
145900 psi

@Treatment Temp. 1600 °F,
Time 8000 hour
Room temp test after thermal exposure
1022 MPa

@Treatment Temp. 871 °C,
Time 1.44e+7 sec
148200 psi

@Treatment Temp. 1600 °F,
Time 4000 hour
Room temp test after thermal exposure
1065 MPa

@Treatment Temp. 871 °C,
Time 3.60e+6 sec
154500 psi

@Treatment Temp. 1600 °F,
Time 1000 hour
Room temp test after thermal exposure
1114 MPa

@Treatment Temp. 871 °C,
Time 360000 sec
161600 psi

@Treatment Temp. 1600 °F,
Time 100 hour
Room temp test after thermal exposure
1161 MPa

@Treatment Temp. 760 °C,
Time 5.76e+7 sec
168400 psi

@Treatment Temp. 1400 °F,
Time 16000 hour
Room temp test after thermal exposure
1191 MPa

@Treatment Temp. 760 °C,
Time 2.88e+7 sec
172700 psi

@Treatment Temp. 1400 °F,
Time 8000 hour
Room temp test after thermal exposure
1205 MPa

@Treatment Temp. 760 °C,
Time 1.44e+7 sec
174800 psi

@Treatment Temp. 1400 °F,
Time 4000 hour
Room temp test after thermal exposure
1223 MPa

@Treatment Temp. 760 °C,
Time 360000 sec
177400 psi

@Treatment Temp. 1400 °F,
Time 100 hour
Room temp test after thermal exposure
1226 MPa

@Treatment Temp. 760 °C,
Time 3.60e+6 sec
177800 psi

@Treatment Temp. 1400 °F,
Time 1000 hour
Room temp test after thermal exposure
1247 MPa

@Treatment Temp. 649 °C,
Time 360000 sec
180900 psi

@Treatment Temp. 1200 °F,
Time 100 hour
Room temp test after thermal exposure
1248 MPa

@Treatment Temp. 649 °C,
Time 3.60e+6 sec
181000 psi

@Treatment Temp. 1200 °F,
Time 1000 hour
Room temp test after thermal exposure
1255 MPa

@Treatment Temp. 649 °C,
Time 1.44e+7 sec
182000 psi

@Treatment Temp. 1200 °F,
Time 4000 hour
Room temp test after thermal exposure
1260 MPa

@Treatment Temp. 649 °C,
Time 5.76e+7 sec
183000 psi

@Treatment Temp. 1200 °F,
Time 16000 hour
Room temp test after thermal exposure
1264 MPa

@Treatment Temp. 649 °C,
Time 2.88e+7 sec
183300 psi

@Treatment Temp. 1200 °F,
Time 8000 hour
Room temp test after thermal exposure
Tensile Strength, Yield 705 MPa
102000 psi
0.2%. Room temp test prior to thermal exposure
452 MPa

@Treatment Temp. 871 °C,
Time 5.76e+7 sec
65600 psi

@Treatment Temp. 1600 °F,
Time 16000 hour
0.2%. Room temp test after thermal exposure
473 MPa

@Treatment Temp. 871 °C,
Time 2.88e+7 sec
68600 psi

@Treatment Temp. 1600 °F,
Time 8000 hour
0.2%. Room temp test after thermal exposure
487 MPa

@Treatment Temp. 871 °C,
Time 1.44e+7 sec
70600 psi

@Treatment Temp. 1600 °F,
Time 4000 hour
0.2%. Room temp test after thermal exposure
533 MPa

@Treatment Temp. 871 °C,
Time 3.60e+6 sec
77300 psi

@Treatment Temp. 1600 °F,
Time 1000 hour
0.2%. Room temp test after thermal exposure
618 MPa

@Treatment Temp. 871 °C,
Time 360000 sec
89600 psi

@Treatment Temp. 1600 °F,
Time 100 hour
0.2%. Room temp test after thermal exposure
658 MPa

@Treatment Temp. 760 °C,
Time 5.76e+7 sec
95400 psi

@Treatment Temp. 1400 °F,
Time 16000 hour
0.2%. Room temp test after thermal exposure
690 MPa

@Treatment Temp. 760 °C,
Time 2.88e+7 sec
100000 psi

@Treatment Temp. 1400 °F,
Time 8000 hour
0.2%. Room temp test after thermal exposure
707 MPa

@Treatment Temp. 760 °C,
Time 1.44e+7 sec
103000 psi

@Treatment Temp. 1400 °F,
Time 4000 hour
0.2%. Room temp test after thermal exposure
742 MPa

@Treatment Temp. 760 °C,
Time 3.60e+6 sec
108000 psi

@Treatment Temp. 1400 °F,
Time 1000 hour
0.2%. Room temp test after thermal exposure
759 MPa

@Treatment Temp. 760 °C,
Time 360000 sec
110000 psi

@Treatment Temp. 1400 °F,
Time 100 hour
0.2%. Room temp test after thermal exposure
798 MPa

@Treatment Temp. 649 °C,
Time 360000 sec
116000 psi

@Treatment Temp. 1200 °F,
Time 100 hour
0.2%. Room temp test after thermal exposure
814 MPa

@Treatment Temp. 649 °C,
Time 3.60e+6 sec
118000 psi

@Treatment Temp. 1200 °F,
Time 1000 hour
0.2%. Room temp test after thermal exposure
816 MPa

@Treatment Temp. 649 °C,
Time 5.76e+7 sec
118000 psi

@Treatment Temp. 1200 °F,
Time 16000 hour
0.2%. Room temp test after thermal exposure
819 MPa

@Treatment Temp. 649 °C,
Time 2.88e+7 sec
119000 psi

@Treatment Temp. 1200 °F,
Time 8000 hour
0.2%. Room temp test after thermal exposure
830 MPa

@Treatment Temp. 649 °C,
Time 1.44e+7 sec
120000 psi

@Treatment Temp. 1200 °F,
Time 4000 hour
0.2%. Room temp test after thermal exposure
Elongation at Break 30 %
30 %
Room temp test prior to thermal exposure
20 %

@Treatment Temp. 760 °C,
Time 2.88e+7 sec
20 %

@Treatment Temp. 1400 °F,
Time 8000 hour
Room temp test after thermal exposure
20 %

@Treatment Temp. 760 °C,
Time 5.76e+7 sec
20 %

@Treatment Temp. 1400 °F,
Time 16000 hour
Room temp test after thermal exposure
21 %

@Treatment Temp. 760 °C,
Time 1.44e+7 sec
21 %

@Treatment Temp. 1400 °F,
Time 4000 hour
Room temp test after thermal exposure
23 %

@Treatment Temp. 649 °C,
Time 5.76e+7 sec
23 %

@Treatment Temp. 1200 °F,
Time 16000 hour
Room temp test after thermal exposure
24 %

@Treatment Temp. 649 °C,
Time 2.88e+7 sec
24 %

@Treatment Temp. 1200 °F,
Time 8000 hour
Room temp test after thermal exposure
26 %

@Treatment Temp. 649 °C,
Time 3.60e+6 sec
26 %

@Treatment Temp. 1200 °F,
Time 1000 hour
Room temp test after thermal exposure
26 %

@Treatment Temp. 649 °C,
Time 1.44e+7 sec
26 %

@Treatment Temp. 1200 °F,
Time 4000 hour
Room temp test after thermal exposure
26 %

@Treatment Temp. 760 °C,
Time 3.60e+6 sec
26 %

@Treatment Temp. 1400 °F,
Time 1000 hour
Room temp test after thermal exposure
27 %

@Treatment Temp. 649 °C,
Time 360000 sec
27 %

@Treatment Temp. 1200 °F,
Time 100 hour
Room temp test after thermal exposure
27 %

@Treatment Temp. 760 °C,
Time 360000 sec
27 %

@Treatment Temp. 1400 °F,
Time 100 hour
Room temp test after thermal exposure
30 %

@Treatment Temp. 871 °C,
Time 3.60e+6 sec
30 %

@Treatment Temp. 1600 °F,
Time 1000 hour
Room temp test after thermal exposure
31 %

@Treatment Temp. 871 °C,
Time 360000 sec
31 %

@Treatment Temp. 1600 °F,
Time 100 hour
Room temp test after thermal exposure
32 %

@Treatment Temp. 871 °C,
Time 1.44e+7 sec
32 %

@Treatment Temp. 1600 °F,
Time 4000 hour
Room temp test after thermal exposure
32 %

@Treatment Temp. 871 °C,
Time 2.88e+7 sec
32 %

@Treatment Temp. 1600 °F,
Time 8000 hour
Room temp test after thermal exposure
33 %

@Treatment Temp. 871 °C,
Time 5.76e+7 sec
33 %

@Treatment Temp. 1600 °F,
Time 16000 hour
Room temp test after thermal exposure
Reduction of Area 33 %
33 %
Room temp test prior to thermal exposure
19 %

@Treatment Temp. 760 °C,
Time 5.76e+7 sec
19 %

@Treatment Temp. 1400 °F,
Time 16000 hour
Room temp test after thermal exposure
21 %

@Treatment Temp. 760 °C,
Time 2.88e+7 sec
21 %

@Treatment Temp. 1400 °F,
Time 8000 hour
Room temp test after thermal exposure
22 %

@Treatment Temp. 760 °C,
Time 1.44e+7 sec
22 %

@Treatment Temp. 1400 °F,
Time 4000 hour
Room temp test after thermal exposure
25 %

@Treatment Temp. 649 °C,
Time 5.76e+7 sec
25 %

@Treatment Temp. 1200 °F,
Time 16000 hour
Room temp test after thermal exposure
27 %

@Treatment Temp. 649 °C,
Time 2.88e+7 sec
27 %

@Treatment Temp. 1200 °F,
Time 8000 hour
Room temp test after thermal exposure
29 %

@Treatment Temp. 649 °C,
Time 3.60e+6 sec
29 %

@Treatment Temp. 1200 °F,
Time 1000 hour
Room temp test after thermal exposure
29 %

@Treatment Temp. 649 °C,
Time 1.44e+7 sec
29 %

@Treatment Temp. 1200 °F,
Time 4000 hour
Room temp test after thermal exposure
29 %

@Treatment Temp. 760 °C,
Time 3.60e+6 sec
29 %

@Treatment Temp. 1400 °F,
Time 1000 hour
Room temp test after thermal exposure
30 %

@Treatment Temp. 760 °C,
Time 360000 sec
30 %

@Treatment Temp. 1400 °F,
Time 100 hour
Room temp test after thermal exposure
30 %

@Treatment Temp. 871 °C,
Time 3.60e+6 sec
30 %

@Treatment Temp. 1600 °F,
Time 1000 hour
Room temp test after thermal exposure
31 %

@Treatment Temp. 649 °C,
Time 360000 sec
31 %

@Treatment Temp. 1200 °F,
Time 100 hour
Room temp test after thermal exposure
31 %

@Treatment Temp. 871 °C,
Time 1.44e+7 sec
31 %

@Treatment Temp. 1600 °F,
Time 4000 hour
Room temp test after thermal exposure
31 %

@Treatment Temp. 871 °C,
Time 2.88e+7 sec
31 %

@Treatment Temp. 1600 °F,
Time 8000 hour
Room temp test after thermal exposure
32 %

@Treatment Temp. 871 °C,
Time 5.76e+7 sec
32 %

@Treatment Temp. 1600 °F,
Time 16000 hour
Room temp test after thermal exposure
36 %

@Treatment Temp. 871 °C,
Time 360000 sec
36 %

@Treatment Temp. 1600 °F,
Time 100 hour
Room temp test after thermal exposure
Modulus of Elasticity 217 GPa

@Temperature 25.0 °C
31500 ksi

@Temperature 77.0 °F
Dynamic
Poissons Ratio 0.319

@Temperature 25.0 °C
0.319

@Temperature 77.0 °F
Shear Modulus 82.0 GPa

@Temperature 25.0 °C
11900 ksi

@Temperature 77.0 °F
Dynamic
Electrical Properties Metric English Comments
Electrical Resistivity 0.0001278 ohm-cm
0.0001278 ohm-cm
0.0001299 ohm-cm
0.0001299 ohm-cm
0.0001299 ohm-cm
0.0001299 ohm-cm
0.0001318 ohm-cm
0.0001318 ohm-cm
0.0001326 ohm-cm
0.0001326 ohm-cm