- HP Alloys Alloy C-276, 50% Cold Worked
HP Alloys Alloy C-276, 50% Cold Worked
| Category | Metal , Nonferrous Metal , Nickel Alloy , Superalloy |
| Manufacturer | High Performance Alloys, Inc |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | HP Alloys Alloy C-276, 50% Cold Worked.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
50% Cold Worked applies to tensile and/or hardness; other properties are typical of this alloy.Data provided by High Performance Alloys, Inc., Allvac, Inco Alloys International, and Haynes International.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 8.90 g/cc | 0.322 lb/in³ |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 1449 MPa | 210200 psi | |
| Tensile Strength, Yield | 1347 MPa | 195400 psi | |
| Elongation at Break | 7.0 % | 7.0 % | |
| Modulus of Elasticity | 205 GPa | 29700 ksi |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 11.7 µm/m-°C @Temperature 20.0 - 100 °C |
6.50 µin/in-°F @Temperature 68.0 - 212 °F |
|
| 12.0 µm/m-°C @Temperature 24.0 - 204 °C |
6.67 µin/in-°F @Temperature 75.2 - 399 °F |
||
| 12.8 µm/m-°C @Temperature 23.9 - 316 °C |
7.11 µin/in-°F @Temperature 75.0 - 600 °F |
||
| 13.2 µm/m-°C @Temperature 23.9 - 427 °C |
7.33 µin/in-°F @Temperature 75.0 - 800 °F |
||
| 13.4 µm/m-°C @Temperature 24.0 - 538 °C |
7.44 µin/in-°F @Temperature 75.2 - 1000 °F |
||
| Specific Heat Capacity | 0.427 J/g-°C | 0.102 BTU/lb-°F | |
| Thermal Conductivity | 10.5 W/m-K | 72.9 BTU-in/hr-ft²-°F | |
| Melting Point | 1325 - 1370 °C | 2417 - 2500 °F | |
| Solidus | 1325 °C | 2417 °F | |
| Liquidus | 1370 °C | 2500 °F |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Carbon, C | <= 0.010 % | <= 0.010 % | |
| Chromium, Cr | 14.5 - 16.5 % | 14.5 - 16.5 % | |
| Cobalt, Co | <= 2.5 % | <= 2.5 % | |
| Iron, Fe | 4.0 - 7.0 % | 4.0 - 7.0 % | |
| Manganese, Mn | <= 1.0 % | <= 1.0 % | |
| Molybdenum, Mo | 15 - 17 % | 15 - 17 % | |
| Nickel, Ni | 57 % | 57 % | |
| Phosphorous, P | <= 0.025 % | <= 0.025 % | |
| Silicon, Si | <= 0.080 % | <= 0.080 % | |
| Sulfur, S | <= 0.010 % | <= 0.010 % | |
| Tungsten, W | 3.0 - 4.5 % | 3.0 - 4.5 % | |
| Vanadium, V | <= 0.35 % | <= 0.35 % |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 0.000130 ohm-cm | 0.000130 ohm-cm | |
| Magnetic Permeability | 1.0002 | 1.0002 | at 200 oersted (15.9 kA/m) |
Users viewing this material also viewed the following:
- Ravago Manufacturing Americas Hylex® P1310G20 HB Polycarbonate, 20% Fiberglass Reinforced, UV Stabilized
- Momentive Performance Materials Siloprenâ„¢ LSR 3486/35 Liquid Silicone Rubber - Self-Lubricating / Low Compression Set
- Solvay Specialty Polymers Algoflon® L600 Polytetrafluoroethylene (PTFE)
- Techmer ES HiFill® HDPE GF25 CC 25% Glass Filled
- Westlake EB171 MDPE Medium Density Polyethylene
- DuPont Teijin Films Teijin® Tetoron® S Polyester Film, 500 Gauge
- ConocoPhillips HD Fleet™ 20W20 Engine Oil
- PolyOne Elastamax XL-0257-2 TPU-Based Thermoplastic Elastomer (discontinued **)
- Kuraray SEPTON® A1 Hot Melt Adhesive
Copyright © lookpolymers.com All Rights Reserved