Seals Eastern 7065 Neoprene / Chloroprene
| Category | Polymer , Thermoset , Rubber or Thermoset Elastomer (TSE) |
| Manufacturer | Seals Eastern, Inc |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Seals Eastern 7065 Neoprene / Chloroprene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
General purpose neopreneInformation provided by Seals Eastern, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.48 g/cc | 1.48 g/cc | ASTM D297, 15 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | >= 77 | >= 77 | ASTM D2240, Type A |
| 82 | 82 | AVG; ASTM D2240, Type A | |
| 87 @Temperature 100 °C, Time 252000 sec |
87 @Temperature 212 °F, Time 70.0 hour |
After Dry Heat Aging; ASTM D865 | |
| Tensile Strength at Break | >= 13.05 MPa | >= 1893 psi | ASTM D412 Method A |
| 16.18 MPa | 2347 psi | AVG; ASTM D412 Method A | |
| 16.18 MPa @Temperature 100 °C, Time 252000 sec |
2347 psi @Temperature 212 °F, Time 70.0 hour |
After Dry Heat Aging; ASTM D865 | |
| Tensile Strength, Yield | >= 2.36 MPa | >= 343 psi | Stress at Elongation M50; ASTM D412 Method A |
| 2.40 MPa | 348 psi | AVG Stress at Elongation M25; ASTM D412 Method A | |
| 3.96 MPa | 574 psi | AVG Stress at Elongation M50; ASTM D412 Method A | |
| >= 5.34 MPa | >= 774 psi | Stress at Elongation M100; ASTM D412 Method A | |
| 8.384 MPa | 1216 psi | AVG Stress at Elongation M100; ASTM D412 Method A | |
| Elongation at Break | >= 126 % | >= 126 % | ASTM D412 Method A |
| 182 % | 182 % | AVG; ASTM D412 Method A | |
| 182 % @Temperature 100 °C, Time 252000 sec |
182 % @Temperature 212 °F, Time 70.0 hour |
After Dry Heat Aging; ASTM D865 | |
| Modulus of Elasticity | 0.01673 GPa | 2.426 ksi | ASTM D412 Method A |
| Shear Modulus | 0.00558 GPa | 0.809 ksi | ASTM D412 Method A |
| Secant Modulus | 0.0157 GPa | 2.28 ksi | ASTM D412 Method A |
| Compression Set | 29 % @Temperature 100 °C, Time 79200 sec |
29 % @Temperature 212 °F, Time 22.0 hour |
ASTM D395, Test B |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Glass Transition Temp, Tg | -40.0 °C | -40.0 °F | ASTM D1329 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Strain Energy / Unit Volume at 20% Elongation (psi) | 39 |
Users viewing this material also viewed the following:
- Parker Chomerics CHO-BOND 1086 Conductive Caulk/Sealant
- Mallard Creek Polymers Rovene® 5051 Styrene-Butadiene Emulsion
- Lehmann & Voss LUVOCOM® 1105-7714 PEEK, with PTFE, lubricant modified, easy flowing
- Lehmann & Voss LUVOCOM® 1-7830 Polyamide 66, with PTFE, lubricant modified, improved wear resistance, high viscosity
- Teknor Apex Telcar® TL-1025-85 Thermoplastic Elastomer
- DSM Arnite® AV2 370 /B PET-35% Glass Reinforced (European and Asian Grade)
- CPC - Vycom SANATEC® Sanitary Cutting Boards High Density Polyethylene
- Eurostar Staramide RF008U PA66/6, 40% Glass Filled, Injection Molded
- Ashley Polymers Ashlene® ABS R214
Copyright © lookpolymers.com All Rights Reserved