H.C. Starck 3402 Molybdenum Alloy AST-4 TZM, Arc-Cast Sheet

Category	Metal , Nonferrous Metal , Molybdenum Alloy
Manufacturer	H.C. Starck
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	H.C. Starck 3402 Molybdenum Alloy AST-4 TZM, Arc-Cast Sheet.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Arc-Cast Sheet 3402Description of Product: This specification covers rolled sheet of carbon-deoxidized TZM alloy (molybdenum + 0.5% titanium + 0.08% zirconium) produced from sheet bar consolidated by the H.C. Stark consumable electrode vacuum-arc-casting process.Structure: Plate will be supplied in a stress-relieved condition unless otherwise requested.Information provided by H.C. Starck.

Mechanical Properties	Metric	English	Comments
Tensile Strength	>= 827 MPa @Thickness 0.254 - 0.635 mm	>= 120000 psi @Thickness 0.0100 - 0.0250 in	ASTM E-8
	>= 827 MPa @Thickness 0.635 - 1.52 mm	>= 120000 psi @Thickness 0.0250 - 0.0600 in	ASTM E-8
	>= 827 MPa @Thickness 1.52 - 2.29 mm	>= 120000 psi @Thickness 0.0600 - 0.0900 in	ASTM E-8
	>= 827 MPa @Thickness 2.29 - 4.75 mm	>= 120000 psi @Thickness 0.0900 - 0.187 in	ASTM E-8
Tensile Strength, Yield	>= 689 MPa @Strain 0.200 %, Thickness 0.254 - 0.635 mm	>= 100000 psi @Strain 0.200 %, Thickness 0.0100 - 0.0250 in	ASTM E-8
	>= 689 MPa @Strain 0.200 %, Thickness 0.635 - 1.52 mm	>= 100000 psi @Strain 0.200 %, Thickness 0.0250 - 0.0600 in	ASTM E-8
	>= 689 MPa @Strain 0.200 %, Thickness 1.52 - 2.29 mm	>= 100000 psi @Strain 0.200 %, Thickness 0.0600 - 0.0900 in	ASTM E-8
	>= 689 MPa @Strain 0.200 %, Thickness 2.29 - 4.75 mm	>= 100000 psi @Strain 0.200 %, Thickness 0.0900 - 0.187 in	ASTM E-8
Elongation at Break	>= 6.0 % @Thickness 0.254 - 0.635 mm	>= 6.0 % @Thickness 0.0100 - 0.0250 in	ASTM E-8
	>= 7.0 % @Thickness 0.635 - 1.52 mm	>= 7.0 % @Thickness 0.0250 - 0.0600 in	ASTM E-8
	>= 9.0 % @Thickness 1.52 - 2.29 mm	>= 9.0 % @Thickness 0.0600 - 0.0900 in	ASTM E-8
	>= 10 % @Thickness 2.29 - 4.75 mm	>= 10 % @Thickness 0.0900 - 0.187 in	ASTM E-8
Bend Radius, Minimum	2.0 t @Thickness <=1.65 mm	2.0 t @Thickness <=0.0650 in	Bend Severity 90Â°, specimens at least 1" by 2", transverse direction

Component Elements Properties	Metric	English	Comments
Carbon, C	0.010 - 0.030 %	0.010 - 0.030 %
Iron, Fe	<= 0.010 %	<= 0.010 %
Molybdenum, Mo	>= 99.25 %	>= 99.25 %	by difference
Nickel, Ni	<= 0.0020 %	<= 0.0020 %
Nitrogen, N	<= 0.0020 %	<= 0.0020 %
Oxygen, O	<= 0.0030 %	<= 0.0030 %
Silicon, Si	<= 0.010 %	<= 0.010 %
Titanium, Ti	0.40 - 0.55 %	0.40 - 0.55 %
Zirconium, Zr	0.060 - 0.12 %	0.060 - 0.12 %