Schmolz + Bickenbach CorroPlast® Plastic Mold Steel

Category	Metal , Ferrous Metal , Tool Steel , Mold Steel
Manufacturer	Schmolz + Bickenbach (Swiss Steel International)
Trade Name	CorroPlast®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Schmolz + Bickenbach CorroPlast® Plastic Mold Steel.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Description: CorroPlast® is a pre-hardened, free-machining 400 series stainless steel, specifically developed for mold bases for processing plastic; and Supplied in the pre-hardened condition with a hardnessCharacteristics: Excellent machinability; Excellent dimensional stability; Good resistance to corrosion (e.g. PVC); Good thermal conductivity; and Good weldabilityApplications: Mold bases for processing corrosive plastics and Mold inserts for processing corrosive plastics with standard requirements for polishability.Information provided by Schmolz + Bickenbach

Physical Properties	Metric	English	Comments
Density	7.70 g/cc	0.278 lb/in³

Mechanical Properties	Metric	English
Hardness, Rockwell C	34	34
Tensile Strength	1100 MPa	160000 psi
Tensile Strength, Yield	889 MPa @Strain 0.200 %	129000 psi @Strain 0.200 %
Elongation at Yield	13 %	13 %

Thermal Properties	Metric	English
CTE, linear	9.00 µm/m-°C @Temperature 21.1 - 93.3 °C	5.00 µin/in-°F @Temperature 70.0 - 200 °F
	10.6 µm/m-°C @Temperature 21.1 - 204 °C	5.90 µin/in-°F @Temperature 70.0 - 400 °F
	11.3 µm/m-°C @Temperature 21.1 - 399 °C	6.30 µin/in-°F @Temperature 70.0 - 750 °F
Thermal Conductivity	21.8 W/m-K @Temperature 21.1 °C	151 BTU-in/hr-ft²-°F @Temperature 70.0 °F
	22.5 W/m-K @Temperature 149 °C	156 BTU-in/hr-ft²-°F @Temperature 300 °F
	23.8 W/m-K @Temperature 343 °C	165 BTU-in/hr-ft²-°F @Temperature 650 °F

Component Elements Properties	Metric	English
Carbon, C	0.050 %	0.050 %
Chromium, Cr	12.5 %	12.5 %
Iron, Fe	86 %	86 %
Manganese, Mn	1.3 %	1.3 %
Sulfur, S	0.15 %	0.15 %