- Sichuan Deyang Haton® hGR50 Polyphenylene Sulfide, Glass Fiber Reinforced
Sichuan Deyang Haton® hGR50 Polyphenylene Sulfide, Glass Fiber Reinforced
| Category | Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) , Polyphenylene Sulfide (PPS) with 50% Glass Fiber Filler |
| Manufacturer | Sichuan Deyang Chemical Co. Ltd. |
| Trade Name | Haton® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Sichuan Deyang Haton® hGR50 Polyphenylene Sulfide, Glass Fiber Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Injection moldingInformation provided by Sichuan Deyang Chemical Co., LTD
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.72 g/cc | 0.0621 lb/in³ | GB/T 1033.1-2008 |
| Water Absorption | 0.020 % | 0.020 % | GB/T 1034-2008 |
| Linear Mold Shrinkage, Flow | 0.0020 cm/cm | 0.0020 in/in | GB/T 15585-1995 |
| Linear Mold Shrinkage, Transverse | 0.0067 cm/cm | 0.0067 in/in | GB/T 15585-1995 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell L | 110 | 110 | GB/T 3398.2-2008 |
| Tensile Strength | 185 MPa | 26800 psi | GB/T 1040.2-2006 |
| Elongation at Break | 1.2 % | 1.2 % | GB/T1040.2-2006 |
| Flexural Strength | 272 MPa | 39500 psi | GB/T 9341-2008 |
| Flexural Modulus | 16.8 GPa | 2440 ksi | GB/T 9341-2008 |
| Izod Impact, Notched (ISO) | 15.0 kJ/m² | 7.14 ft-lb/in² | GB/T 1843-2008 |
| Izod Impact, Unnotched (ISO) | 46.0 kJ/m² | 21.9 ft-lb/in² | GB/T 1843-2008 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 280 °C | 536 °F | GBT/T 19466.3-2004 |
| Deflection Temperature at 1.8 MPa (264 psi) | 268 °C | 514 °F | GB/T 1634.2-2004 |
| Flammability, UL94 | V-0 | V-0 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 2.00e+16 ohm-cm | 2.00e+16 ohm-cm | GB/T1410-2006 |
| Surface Resistivity per Square | 8.00e+15 ohm | 8.00e+15 ohm | GB/T1410-2006 |
| Dielectric Constant | 4.0 | 4.0 | GB/T 1409-2006 |
| Dielectric Strength | 16.0 kV/mm | 406 kV/in | GB/T1408.1-2006 |
| Dissipation Factor | 0.0010 | 0.0010 | GB/T 1409-2006 |
Users viewing this material also viewed the following:
- Plastcom PLASTAMID® 66 BT N 27 B PA66
- MV Labs NA790 NaNO2 Sodium nitrite
- SABIC Innovative Plastics Lexan® HFD1232 PC Copolymer
- KKPC Kumho KHS 65P High Styrene Resin Masterbatch (HSR)
- Barlog Plastics KEBAFORM C 901 SO POM Copolymer unreinforced, improved wear and friction
- Carpenter Micro-Melt® 9 Wear Treated Tool Steel
- Zircar Zirconia ZOF-100 Pure Zirconia Felt Insulation
- BASF 3-Dimethylaminopropane-1-ol
Copyright © lookpolymers.com All Rights Reserved