Gouda Vuurvast CURON 160 H Dense Refractory Castable

Category	Ceramic , Oxide , Aluminum Oxide , Silicon Oxide
Manufacturer	Gouda Vuurvast
Trade Name	CURON
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Gouda Vuurvast CURON 160 H Dense Refractory Castable.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Description: Because of the selection of raw materials this castable has a high volume stability and keeps its strength up to high temperatures. In addition Curon 160 H has an excellent thermal shock resistance. It is largely used in the steel industry.Remarks: These values apply to cast products. Also available in gunning variety, marked "GM".Information provided by Gouda Vuurvast.

Physical Properties	Metric	English	Comments
Bulk Density	2.30 - 2.40 g/cc	0.0831 - 0.0867 lb/inÂ³	After drying at 110Â°C
Particle Size	<= 6000 Âµm	<= 6000 Âµm	Grain Size

Mechanical Properties	Metric	English	Comments
Compressive Strength	40.0 - 50.0 MPa @Temperature 1300 Â°C	5800 - 7250 psi @Temperature 2370 Â°F	Cold Crushing Strength
	55.0 - 65.0 MPa @Temperature 100 Â°C	7980 - 9430 psi @Temperature 212 Â°F	Cold Crushing Strength

Thermal Properties	Metric	English	Comments
Thermal Conductivity	0.640 - 0.740 W/m-K @Temperature 100 Â°C	4.44 - 5.14 BTU-in/hr-ftÂ²-Â°F @Temperature 212 Â°F
	0.640 - 0.740 W/m-K @Temperature 600 Â°C	4.44 - 5.14 BTU-in/hr-ftÂ²-Â°F @Temperature 1110 Â°F
	0.770 - 0.870 W/m-K @Temperature 1300 Â°C	5.34 - 6.04 BTU-in/hr-ftÂ²-Â°F @Temperature 2370 Â°F
Maximum Service Temperature, Air	1600 Â°C	2910 Â°F
Shrinkage	-0.250 - 0.250 % @Temperature 1300 Â°C	-0.250 - 0.250 % @Temperature 2370 Â°F	Permanent Linear Change

Component Elements Properties	Metric	English
Al2O3	64 %	64 %
Fe2O3	<= 1.5 %	<= 1.5 %
SiO2	30 %	30 %

Descriptive Properties	Value	Comments
ASTM Classification	E
Material Consumption per 1 m3	2250 kg
Mixing Water	8-10 liters	per 100 kgs dry material