Goodfellow Cobalt/Silicon/Boron/Manganese Alloy
| Category | Metal , Electronic/Magnetic Alloy , Nonferrous Metal , Cobalt Alloy |
| Manufacturer | Goodfellow |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Goodfellow Cobalt/Silicon/Boron/Manganese Alloy.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Goodfellow.Composition Notes: Si + B content = 25 wt%. Fe+Mo content = 2 wt%.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 7.60 g/cc | 0.275 lb/in³ |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Vickers Microhardness | 900 | 900 | kg(f)/mm² |
| Tensile Strength at Break | 1500 - 2000 MPa | 218000 - 290000 psi | |
| Tensile Modulus | 150 GPa | 21800 ksi |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Crystallization Temperature | 450 °C | 842 °F | |
| Maximum Service Temperature, Air | 80.0 - 120 °C | 176 - 248 °F |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Cobalt, Co | 70 % | 70 % | |
| Manganese, Mn | 5.0 % | 5.0 % |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 0.000130 ohm-cm | 0.000130 ohm-cm | |
| Magnetic Coercive Force, Hc | 0.013 Oe | 0.013 Oe | |
| Magnetic Saturation Flux Density, Bmax | 8000 Gauss | 8000 Gauss | |
| Magnetic Remanence, Br | 0.70 - 0.95 Gauss | 0.70 - 0.95 Gauss | Remanence Ratio, B<sub>r</sub>/B<sub>s</sub> |
| Curie Temperature | 350 °C | 662 °F |
Users viewing this material also viewed the following:
- 3M Scotch-Weld™ 3535 B/A Off-white Two-Part Urethane Adhesive 3535 B/A Off-white (discontinued **)
- Momentive Performance Materials TUFELâ„¢ II 94505 Low Volatile Extrusion Heat Cured Rubber
- SABIC Innovative Plastics Noryl V01505 PPE+HIPS
- SK Chemicals SKYPEL P147D Productivity Grade
- A. Schulman POLYFORT™ PP 1930UX Extra High Flow, UV Stabilized Copolymer Polypropylene
- Arlon 56141R025 0.025" (0.635 mm) Uncured Silicone Rubber with Fiberglass Substrate
- 3A Composites Core Materials BALTEK® SB.50 Structural End-Grain Balsa
- Formosa Plastics Formolene® L64220U Rotational Molding LLDPE (discontinued **)
Copyright © lookpolymers.com All Rights Reserved