- GEHR Plastics Noryl PPO-30 GF 30% Glass Filled (discontinued **)
GEHR Plastics Noryl PPO-30 GF 30% Glass Filled (discontinued **)
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polyphenylene Ether, 30% Glass Filled |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | GEHR Plastics Noryl PPO-30 GF 30% Glass Filled
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PPO-30 GF is reinforced with 30% glass fiber for higher thermal properties and better dimensional stability. PPO belongs to the group of the amorphous materials and can be used in temperatures ranging from -58 °F to +302 °F. PPO exhibits a high impact strength and a very high dimensional stability. The electrical properties will not be influenced by the surrounding frequencies and therefore can be used in a lot of applications in electrical engineering.
Main Characteristics: high dimensional stability; low tendency to creep; high thermostability; high impact strength; good electrical characteristics over a far frequency range; high resistance to hydrolysis; self-extinguishingInformation provided by GEHR Plastics, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.31 g/cc | 1.31 g/cc | ASTM D792 |
| Water Absorption | 0.0060 % | 0.0060 % | ASTM D570 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell L | 108 | 108 | ASTM D785 |
| Tensile Strength at Break | 121 MPa | 17500 psi | ASTM D1708 |
| Elongation at Break | 5.0 % | 5.0 % | ASTM D1708 |
| Modulus of Elasticity | 7.79 GPa | 1130 ksi | ASTM D638 |
| Flexural Strength | 172 MPa | 25000 psi | ASTM D 790 |
| Izod Impact, Notched (ISO) | 4.62 kJ/m² | 2.20 ft-lb/in² | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 0.702 µm/m-°C | 0.390 µin/in-°F | ASTM D696 |
| Maximum Service Temperature, Air | 110 °C | 230 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 135 °C | 275 °F | HDT/A; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 141 °C | 285 °F | HDT/B; ASTM D648 |
| Minimum Service Temperature, Air | -50.0 °C | -58.0 °F | |
| Flammability, UL94 | V-1 | V-1 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | ASTM D257 |
| Surface Resistivity per Square | 1.00e+14 ohm | 1.00e+14 ohm | ASTM D257 |
| Dielectric Strength | 20.9 kV/mm | 530 kV/in | ASTM D139 |
| Comparative Tracking Index | 325 V | 325 V | VDE 0303 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Acid Resistance | Yes | |
| Aromatic Resistance | No | |
| Bondability | Yes | |
| CKW Resistance | No | |
| Hydrocarbonate Resistance | Limited | |
| Hydroxide Resistance | Yes | |
| Ketone Resistance | No | |
| Physiological indifference according | On Request | |
| Resistance to Hot Water | Yes | |
| UV Stabilization | Limited |
Users viewing this material also viewed the following:
- TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, 0.5 PHR Sulfur
- Hybrid Plastics Fireban® Mark VI Resorcinolinic (PRF)
- Saint-Gobain Norton® T-200 Mechanical Grade PTFE Sheet (0.062" thick)
- Borealis LE0563 Polyethylene Compound, Thermoplastic, Semiconductive
- Lubrizol ESTANE® 5715 Ester Based Thermoplastic Polyurethane (European Grade)
- Domo 2600TC Polypropylene Copolymer
- Dow CYCLOTENE™ XU35132 Advanced Electronic Resins (PhotoBisbenzocyclobutene BCB)
- 3M AC-350 Class C-1/2 Aerospace Sealant
Copyright © lookpolymers.com All Rights Reserved