Material Notes:
Sarcon HR is Fujipolys originally developed High Heat Conductive Silicone Rubber. Fine, high heat conductive ceramic particles are mixed with insulative silicone rubber.Sarcon GHR is a composite of Heat Conductive Silicone Rubber and fiberglass.Information provided by Fujipoly Industries
Mechanical Properties Metric English Comments
Hardness, Shore A 92
92
ASTM D2240
92
92
150°C for 1,000 hrs; ASTM D2240
92
92
60°C for 500 hrs; ASTM D2240
94
94
200°C for 1,000 hrs; ASTM D2240
Tensile Strength, Yield 39.33 MPa
5704 psi
200°C for 1,000 hrs
52.0 MPa
7540 psi
150°C for 1,000 hrs; ASTM D1458
53.3 MPa
7730 psi
ASTM D1458
Elongation at Yield <= 2.0 %
<= 2.0 %
ASTM D1458
<= 2.0 %
<= 2.0 %
150°C for 1,000 hrs; ASTM D1458
<= 2.0 %
<= 2.0 %
200°C for 1,000 hrs; ASTM D1458
Thermal Properties Metric English Comments
Maximum Service Temperature, Air 182 °C
360 °F
Minimum Service Temperature, Air -60.0 °C
-76.0 °F
Flammability, UL94 V-0
V-0
Electrical Properties Metric English Comments
Volume Resistivity 3.20e+12 ohm-cm
3.20e+12 ohm-cm
60°C for 500 hrs
1.00e+15 ohm-cm
1.00e+15 ohm-cm
1.80e+16 ohm-cm
1.80e+16 ohm-cm
150°C for 1,000 hrs
1.80e+16 ohm-cm
1.80e+16 ohm-cm
200°C for 1,000 hrs
Dielectric Constant 2.4

@Frequency 50 Hz
 2.4

@Frequency 50 Hz
 After 1000 hrs at 200°C
2.4

@Frequency 1000 Hz
 2.4

@Frequency 1000 Hz
 After 1000 hrs at 200°C
2.4

@Frequency 1e+6 Hz
 2.4

@Frequency 1e+6 Hz
 After 1000 hrs at 200°C
2.5

@Frequency 1000 Hz
 2.5

@Frequency 1000 Hz
 After 1000 hrs at 150°C
2.5

@Frequency 1e+6 Hz
 2.5

@Frequency 1e+6 Hz
 After 1000 hrs at 150°C
2.5

@Frequency 50 Hz
 2.5

@Frequency 50 Hz
 After 1000 hrs at 150°C
3.0

@Frequency 1000 Hz
 3.0

@Frequency 1000 Hz
3.0

@Frequency 50 Hz
 3.0

@Frequency 50 Hz
3.0

@Frequency 1e+6 Hz
 3.0

@Frequency 1e+6 Hz
3.3

@Frequency 1e+6 Hz
 3.3

@Frequency 1e+6 Hz
 After 500 hrs at 60°C
3.3

@Frequency 1000 Hz
 3.3

@Frequency 1000 Hz
 After 500 hrs at 60°C
3.5

@Frequency 50 Hz
 3.5

@Frequency 50 Hz
 After 500 hrs at 60°C
Dielectric Strength 2.50 kV/mm
63.5 kV/in
200°C for 1,000 hrs
2.50 kV/mm
63.5 kV/in
60°C for 500 hrs
3.00 kV/mm
76.2 kV/in
AC 60 Hz
3.00 kV/mm
76.2 kV/in
150°C for 1,000 hrs
Dielectric Breakdown 2000 V
2000 V
Withstand Voltage [V/min]; AC 60 Hz
Dissipation Factor 0.0010

@Frequency 1000 Hz
 0.0010

@Frequency 1000 Hz
 After 1000 hrs at 200°C
0.0020

@Frequency 50 Hz
 0.0020

@Frequency 50 Hz
 After 1000 hrs at 200°C
0.0020

@Frequency 1000 Hz
 0.0020

@Frequency 1000 Hz
 After 1000 hrs at 150°C
0.0030

@Frequency 1e+6 Hz
 0.0030

@Frequency 1e+6 Hz
 After 1000 hrs at 150°C
0.0030

@Frequency 1e+6 Hz
 0.0030

@Frequency 1e+6 Hz
 After 1000 hrs at 200°C
0.0030

@Frequency 1e+6 Hz
 0.0030

@Frequency 1e+6 Hz
0.0040

@Frequency 50 Hz
 0.0040

@Frequency 50 Hz
 After 1000 hrs at 150°C
0.0050

@Frequency 1000 Hz
 0.0050

@Frequency 1000 Hz
0.0070

@Frequency 1e+6 Hz
 0.0070

@Frequency 1e+6 Hz
 After 500 hrs at 60°C
0.010

@Frequency 1000 Hz
 0.010

@Frequency 1000 Hz
 After 500 hrs at 60°C
0.015

@Frequency 50 Hz
 0.015

@Frequency 50 Hz
0.045

@Frequency 50 Hz
 0.045

@Frequency 50 Hz
 After 500 hrs at 60°C
Descriptive Properties Value Comments
Color Brown
Thermal Impedance 0.55°C/W
FTM P-3010; ASTM D5470
Thermal Impedance AD Type 0.63°C/W
FTM P-3010; ASTM D5470