Formosa Plastics Formolene® HB5502F Blow Molding HDPE

Category	Polymer , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Blow Molding Grade
Manufacturer	Formosa Plastics Corporation, USA
Trade Name	Formolene®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Formosa Plastics Formolene® HB5502F Blow Molding HDPE.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

High Density Polyethylene Hexene Copolymer with Synthetic Antistat Formolene® HB5502F HDPE resin is designed for applications requiring excellent stiffness and stress crack resistance properties. It may be used as a blow molding resin or sheet extrusion thermoforming resin.Formolene® HB5502F meets all requirements of the U.S. Food and Drug Administration as specified in 21 CFR 177.1520, covering safe use of polyolefin articles intended for direct food contact.Applications: Blow molding – Pharmaceuticals, Food Packaging, Industrial Chemicals and Industrial Parts; Molding or Forming - Industrial Parts and PalletsPhysical properties reported herein were determined on compression molded specimens prepared in accordance with Procedure C of ASTM D1928.Information provided by Formosa Plastics Corporation, USA

Physical Properties	Metric	English	Comments
Density	0.954 g/cc	0.0345 lb/in³	ASTM D1505
ESCR 100% Igepal®	30 hour	30 hour	Condition B, F<sub>50</sub>; ASTM D1693
Melt Flow	0.35 g/10 min @Load 2.16 kg, Temperature 190 °C	0.35 g/10 min @Load 4.76 lb, Temperature 374 °F	Condition E; ASTM D1238

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	27.6 MPa	4000 psi	2" (50mm) per min, Type IV; ASTM D638
Elongation at Break	>= 600 %	>= 600 %	2" (50mm) per min, Type IV; ASTM D638
Flexural Modulus	1.03 GPa	150 ksi	ASTM D790

Thermal Properties	Metric	English	Comments
Brittleness Temperature	<= -84.0 °C	<= -119 °F	ASTM D746