- Fiberfil® J-68/20/E/SD/HM Polypropylene Copolymer, 20% Glass Fiber Reinforced, Chemically coupled, with static dissipation
Fiberfil® J-68/20/E/SD/HM Polypropylene Copolymer, 20% Glass Fiber Reinforced, Chemically coupled, with static dissipation
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | FiberFil |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Fiberfil® J-68/20/E/SD/HM Polypropylene Copolymer, 20% Glass Fiber Reinforced, Chemically coupled, with static dissipation.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by FIBERFIL Engineered Plastics
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.04 g/cc | 1.04 g/cc | ASTM D792 |
| Water Absorption | 0.020 % | 0.020 % | 24 hr; ASTM D570 |
| Linear Mold Shrinkage | 0.0020 - 0.0030 cm/cm @Thickness 3.17 mm |
0.0020 - 0.0030 in/in @Thickness 0.125 in |
ASTM D955 |
| 0.0030 - 0.0040 cm/cm @Thickness 6.35 mm |
0.0030 - 0.0040 in/in @Thickness 0.250 in |
ASTM D955 | |
| Melt Flow | 12 g/10 min | 12 g/10 min | 230/2.16 (typical); ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 90 | 90 | ASTM D785 |
| Tensile Strength, Yield | 42.0 MPa | 6090 psi | ASTM D638 |
| Elongation at Yield | 4.0 % | 4.0 % | ASTM D638 |
| Tensile Modulus | 2.69 GPa | 390 ksi | ASTM D638 |
| Flexural Strength | 56.0 MPa | 8120 psi | ASTM D790 |
| Flexural Modulus | 2.65 GPa | 384 ksi | Tangent; ASTM D790 |
| Izod Impact, Notched | 1.23 J/cm @Thickness 3.17 mm |
2.30 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 136 °C | 276 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 129 °C | 265 °F | ASTM D648 |
Users viewing this material also viewed the following:
- Old Hickory S-4 Tennessee Ball Clay
- Precision Polymer Engineering J80P Butyl Rubber
- Polykemi AB POLYfill PPHC TS25020 Polypropylene, Mineral Reinforced
- Nilit FRIANYL A63 CV10 Nylon 6.6 for injection molding, 10% carbon fiber reinforced
- SABIC Innovative Plastics Lexan® EXL1414H PC Copolymer (Asia Pacific)
- LyondellBasell Petrothene® M2520FN Low Density Polyethylene
- SABIC Innovative Plastics NORYL HN731SE PPE+HIPS (Europe-Africa-Middle East)
- Chosun Refractories LW-30 Special Insulating Firebrick
- PolyOne Synprene® RT-5190 Thermoplastic Elastomer - SBC (discontinued **)
Copyright © lookpolymers.com All Rights Reserved