DuPont™ Tedlar® TWH15BL3 Low Gloss White Polyvinyl Fluoride Film

Category Polymer , Film , Thermoplastic , Fluoropolymer
Manufacturer DuPont
Trade Name Tedlar®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont™ Tedlar® TWH15BL3 Low Gloss White Polyvinyl Fluoride Film.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Properties of DuPont™ Tedlar® polyvinyl fluoride (PVF) biaxially oriented film include excellent resistance to weathering, outstanding mechanical properties, and inertness towards a wide variety of chemicals, solvents, and staining agents.Information provided by DuPont.
Physical Properties Metric English Comments
Specific Gravity 1.46 g/cc
1.46 g/cc
ASTM D1505
Moisture Absorption at Equilibrium <= 0.50 %
<= 0.50 %
ASTM D570
Moisture Vapor Transmission 0.930 cc-mm/m²-24hr-atm
2.36 cc-mil/100 in²-24hr-atm
ASTM E96
Thickness 38.1 microns
1.50 mil
Mechanical Properties Metric English Comments
Film Elongation at Break, MD >= 90 %
>= 90 %
ASTM D882
Secant Modulus, MD 2.10 GPa
305 ksi
ASTM D822
Impact 42.7
42.7
kJ/m; Spencer; ASTM D3420
Coefficient of Friction 0.18
0.18
Film:Metal; ASTM D1894
Tear Strength 102 kN/m
582 pli
Graves (initial), TD; ASTM D1004
129 kN/m
736 pli
Graves (initial), MD; ASTM D1004
Elmendorf Tear Strength, MD 0.909 g/micron
23.1 g/mil
ASTM D1922
Elmendorf Tear Strength, TD 0.732 g/micron
18.6 g/mil
ASTM D1922
Film Tensile Strength at Break, MD >= 55.2 MPa
>= 8000 psi
ASTM D882
Thermal Properties Metric English Comments
CTE, linear 67.0 µm/m-°C

@Temperature 50.0 - 70.0 °C
37.2 µin/in-°F

@Temperature 122 - 158 °F
MD; ASTM D696
80.0 µm/m-°C

@Temperature 50.0 - 70.0 °C
44.4 µin/in-°F

@Temperature 122 - 158 °F
TD; ASTM D696
Specific Heat Capacity 1.09 J/g-°C
0.261 BTU/lb-°F
DuPont 990 test
Maximum Service Temperature, Air 107 °C
225 °F
Continuous
175 °C
347 °F
Short Cycle
Minimum Service Temperature, Air -72.0 °C
-97.6 °F
Continuous
Shrinkage <= 5.0 %

@Temperature 170 °C
<= 5.0 %

@Temperature 338 °F
TD; ASTM D1204
Optical Properties Metric English Comments
Refractive Index 1.46

@Temperature 30.0 °C
1.46

@Temperature 86.0 °F
n<sub>D</sub>; Abbe Refractometer; ASTM D-542
Descriptive Properties Value Comments
Aging in Air > 3000 hours to embrittlement
300°F Oven