Fainplast Compounds RH 225 Rigid PVC, Antishock Extrusion
| Category | Polymer , Thermoplastic , Vinyl (PVC) , PVC, Extruded |
| Manufacturer | Fainplast Compounds |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Fainplast Compounds RH 225 Rigid PVC, Antishock Extrusion.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Antishock pipes and profiles
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.53 - 1.57 g/cc | 0.0553 - 0.0567 lb/in³ | ISO R 1184 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 37.0 MPa | 5370 psi | ISO R 527 |
| Tensile Strength, Yield | 40.0 MPa | 5800 psi | ISO R527 |
| Elongation at Break | 120 % | 120 % | ISO R 527 |
| Izod Impact, Unnotched | 1.60 - 2.00 J/cm @Temperature 23.0 °C |
3.00 - 3.75 ft-lb/in @Temperature 73.4 °F |
ISO R180 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Vicat Softening Point | 82.0 - 84.0 °C @Load 5.00 kg |
180 - 183 °F @Load 11.0 lb |
ISO R306 |
Users viewing this material also viewed the following:
- Ovation Polymers Opnyl OP6GF15 Nylon 6, 15% Glass Reinforced, Conditioned
- Northstar Polymers MSB-M25B Microcellular Foam based on High Performance Polyester Polyurethane
- Haynes 188 alloy, 20% cold reduction, 3.2 mm thick sheet, 1175°C for 5 minutes
- Haynes 230® alloy, 10% cold reduction
- SABIC Innovative Plastics Ultem 1100EF PEI (Europe-Africa-Middle East)
- SABIC Innovative Plastics LNP LUBRICOMP WFL369 PBT (Europe-Africa-Middle East)
- Techmer ES Statiblend® 02056 Polypropylene
- Westlake EMAC® SP2268 24% Ethylene-Methyl Acrylate Copolymer
- Hexcel® HexForce™ 5352 Aramid Fabric
- Eurostar Starpylen HU 30BF4 PP, 30% Bamboo Fiber Filled, Injection Molding
Copyright © lookpolymers.com All Rights Reserved