ExxonMobil Oppalyte™ 30MW648 OPP Film

Category	Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Film Grade
Manufacturer	Exxon Chemical
Trade Name	Oppalyte™
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	ExxonMobil Oppalyte™ 30MW648 OPP Film.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Product Description: A high speed super white opaque, biaxially oriented polypropylene film coated one side acrylic, one side very low temperature seal (VTLS) coating. VLTS coating provides an excellent performance on high speed HFFS machines. Acrylic provides a good aroma barrier and an excellent surface for printability.Availability: Africa & Middle East, Asia Pacific and EuropeKey Features:Exceptional wide sealing range with a low minimum seal temperature (MST)Excellent seal strength and hot-tackRobust performance on horizontal flow pack machinesExcellent humidity seal retention on VLTS sideGood aroma barrierOutstanding opacity, white background and reduced show throughHigh yieldIdeal support for normal ink systemsWater-based coatingsFeatures:Acrylic CoatedFlavor & Aroma BarrierHumidity ResistantLight BarrierVery Broad Seal RangeVLTS CoatedApplications:BakeryBiscuits/Cookie/Crackers Confectionery, ChocolateConfectionery, GumConfectionery, SugarCrisps and SnacksDry Foods and Beverage PowdersFresh ProduceFrozen FoodHealth and Beauty CareHousehold DetergentsIce CreamPet Food Uses: HFFS Flexible Packaging Processing Method: Inner Web Adhesive Lamination, Solvent Flexographic Printing and Surface Print UnsupportedInformation provided by ExxonMobil

Physical Properties	Metric	English	Comments
Water Vapor Transmission	1.40 g/m²/day @Temperature 23.0 °C	0.0900 g/100 in²/day @Temperature 73.4 °F	85% RH; ExxonMobil Method
	6.98 g/m²/day @Temperature 38.0 °C	0.450 g/100 in²/day @Temperature 100 °F	90% RH; ExxonMobil Method
Oxygen Transmission Rate	1000 cc/m²/day @Temperature 23.0 °C	64.5 cc/100 in²/day @Temperature 73.4 °F	Wet, 75% RH; ExxonMobil Method
	1010 cc/m²/day @Temperature 23.0 °C	65.0 cc/100 in²/day @Temperature 73.4 °F	0% RH; ExxonMobil Method
Thickness	30.5 microns	1.20 mil	ExxonMobil Method
Coating Weight	19.0 g/m²	11.9 lb/ream	ExxonMobil Method

Mechanical Properties	Metric	English	Comments
Film Elongation at Break, MD	140 %	140 %	7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
Film Elongation at Break, TD	50 %	50 %	7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
Modulus of Elasticity	1.30 GPa	189 ksi	MD; ExxonMobil Method
	2.10 GPa	305 ksi	TD; ExxonMobil Method
Coefficient of Friction	0.25	0.25	Acrylic; ExxonMobil Method
	0.50	0.50	VLTS; ExxonMobil Method
Seal Strength	410 g/25 mm @Pressure 0.138 MPa, Temperature 80.0 °C	410 g/in @Pressure 20.0 psi, Temperature 176 °F	LTS, 0.8 sec; ExxonMobil Method
Film Tensile Strength at Break, MD	100 MPa	14500 psi	7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
Film Tensile Strength at Break, TD	155 MPa	22500 psi	7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method

Thermal Properties	Metric	English	Comments
Shrinkage, MD	6.0 % @Temperature 135 °C, Time 432 sec	6.0 % @Temperature 275 °F, Time 0.120 hour	ExxonMobil Method
Shrinkage, TD	6.0 % @Temperature 135 °C, Time 432 sec	6.0 % @Temperature 275 °F, Time 0.120 hour	ExxonMobil Method

Optical Properties	Metric	English	Comments
Gloss	75 %	75 %	45°; ExxonMobil Method
Transmission, Visible	26 %	26 %	ExxonMobil Method

Descriptive Properties	Value	Comments
Heat Seal Range	126°F	VLTS, 36.3 psi, 0.2 sec
Whiteness Index	78
Yield	36500 in²/lb