Polyram PlusTek PB826G3 Nylon 6 for Injection Molding, 15% Glass-fiber Reinforced, Impact Modified and UV Stabilized
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Impact Grade |
| Manufacturer | Polyram |
| Trade Name | PlusTek |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polyram PlusTek PB826G3 Nylon 6 for Injection Molding, 15% Glass-fiber Reinforced, Impact Modified and UV Stabilized.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
15% Glass fiber reinforced, impact modified and UV stabilized Nylon 6 for injection molding applications.Information provided by Polyram.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.18 g/cc | 0.0426 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 2.5 % | 2.5 % | 50% RH; ISO 62 |
| Water Absorption at Saturation | 7.3 % | 7.3 % | ISO 62 |
| Linear Mold Shrinkage | 0.0040 - 0.0070 cm/cm | 0.0040 - 0.0070 in/in | ISO 2577 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 85 | 85 | |
| Tensile Strength, Yield | 100 MPa | 14500 psi | ISO 527 |
| Elongation at Break | 3.5 % | 3.5 % | ISO 527 |
| Tensile Modulus | 4.90 GPa | 711 ksi | ISO 527 |
| Flexural Strength | 150 MPa | 21800 psi | ISO 178 |
| Flexural Modulus | 4.20 GPa | 609 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 15.0 kJ/m² @Temperature 23.0 °C |
7.14 ft-lb/in² @Temperature 73.4 °F |
ISO 180 |
| Charpy Impact Unnotched | 7.00 J/cm² @Temperature -70.0 °C |
33.3 ft-lb/in² @Temperature -94.0 °F |
ISO 179 |
| 7.20 J/cm² @Temperature 23.0 °C |
34.3 ft-lb/in² @Temperature 73.4 °F |
ISO 179 | |
| Charpy Impact, Notched | 0.800 J/cm² @Temperature -30.0 °C |
3.81 ft-lb/in² @Temperature -22.0 °F |
ISO 179 |
| 2.00 J/cm² @Temperature 23.0 °C |
9.52 ft-lb/in² @Temperature 73.4 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 218 °C | 424 °F | ISO 11357 |
| Maximum Service Temperature, Air | 110 °C | 230 °F | Continuous use |
| 200 °C | 392 °F | Short peaks operation | |
| Deflection Temperature at 0.46 MPa (66 psi) | 210 °C | 410 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 170 °C | 338 °F | ISO 75 |
| Vicat Softening Point | 215 °C | 419 °F | ISO 306 |
| Flammability, UL94 | HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
|
| Flame Spread | 20 mm/min | 0.79 in/min | FMVSS302 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+10 ohm-cm | 1.00e+10 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+10 ohm | 1.00e+10 ohm | IEC 60093 |
| Dielectric Strength | 80.0 kV/mm | 2030 kV/in | IEC 60250 |
Users viewing this material also viewed the following:
- Nabaltec APYRAL® 120E Al(OH)3
- DuPont Bynel® E403 Acid-Modified Ethylene Terpolymer Adhesive Resin (discontinued **)
- Techmer ES HiFill® PA4/6 GF25 HS NAT 25% Glass Filled (Conditioned)
- SABIC Innovative Plastics LNP THERMOCOMP HB006 PA11
- A. Schulman PP 3487-01 Polypropylene Homopolymer Polypropylene
- Total MDPE HL 323 Medium Density Polyethylene, Film Resin
- Colorite Polymers 1104 Clear Extrusion Vinyl Compound
- 3M AC-350 Class B-12 Aerospace Sealant
- ATI Allegheny Ludlum Martensitic Stainless Steel Type 440A, Hardened + 204°C Temper
- Resinlab® TL5071 Anaerobic Threadlocking Compound
Copyright © lookpolymers.com All Rights Reserved