ExxonMobil Label-Lyte™ 33LL247 OPP Film
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Film Grade |
| Manufacturer | Exxon Chemical |
| Trade Name | Label-Lyte™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | ExxonMobil Label-Lyte™ 33LL247 OPP Film.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Product Description: A super white opaque, high gloss, caviated BOPP film designed for use in reel-fed warp-around labeling applications where superior graphics are desired.Availability: Africa & Middle East, Asia Pacific and EuropeKey Features:Outstanding opacity and whiteness Superb glossExceptional printabilityExcellent hot melt anchorageExcellent stiffnessExcellent machine performanceHigh tear and split resistanceHigh resistance to elongation on labeling machineGood mold resistance Applications:Beverage, AlcoholicBeverage, Carbonated Beverage, Mineral Waters Dairy ProductsHealth and Beauty CareHousehold and DetergentsIndustrialUses: Reel-Fed LabelsProcessing Method: Inner Web Adhesion Lamination, Solvent Flexographic Printing, Solvent Rotogravure Printing, Surface Print Unsupported, UV Flexographic Printing and UV Offset Lithography PrintingInformation provided by ExxonMobil
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Thickness | 33.0 microns | 1.30 mil | ExxonMobil Method |
| Coating Weight | 20.2 g/m² | 12.6 lb/ream | ExxonMobil Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Elongation at Break, MD | 140 % | 140 % | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
| Film Elongation at Break, TD | 50 % | 50 % | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
| Modulus of Elasticity | 1.30 GPa | 189 ksi | MD; ExxonMobil Method |
| 2.10 GPa | 305 ksi | TD; ExxonMobil Method | |
| Coefficient of Friction | 0.60 | 0.60 | Untreated Surface; ExxonMobil Method |
| Film Tensile Strength at Break, MD | 100 MPa | 14500 psi | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
| Film Tensile Strength at Break, TD | 155 MPa | 22500 psi | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Shrinkage, MD | 6.0 % @Temperature 135 °C, Time 432 sec |
6.0 % @Temperature 275 °F, Time 0.120 hour |
ExxonMobil Method |
| Shrinkage, TD | 6.0 % @Temperature 135 °C, Time 432 sec |
6.0 % @Temperature 275 °F, Time 0.120 hour |
ExxonMobil Method |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Gloss | 75 % | 75 % | 45°; ExxonMobil Method |
| Transmission, Visible | 22 % | 22 % | ExxonMobil Method |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Whiteness Index | 90 | |
| Yield | 34300 in2/lb |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics LNP LUBRICOMP DFP36 PC
- Kazanorgsintez 153-21 Composition of Low Density Polyethylene, Crack-Proof
- Lucas-Milhaupt EASY FLO 30 Silver Based Cadmium-Bearing Filler Metal
- Saint-Gobain CHR® 2345-5 Polyimide Film Backing Silicone Adhesive Pressure Sensitive Tape
- Plastics Group Polifil® GFABS-20 20% Glass-Reinforced Acrylonitrile-Butadiene Styrene (ABS)
- A. Schulman INVISION™ VX-5075UI Soft Touch Polyolefin Thermoplastic
- Covestro Baydur® 646 Polyurethane Structural Foam RIM, Density 25 pcf, MDI-based 2-Component Liquid System
- Dow Corning 3-4154 DIELECTRIC GEL KIT
- 3M Hi-Strength 94 ET Spray Adhesive-Low VOC
Copyright © lookpolymers.com All Rights Reserved