ExxonMobil Oppalyte™ 38MW247 OPP Film
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Film Grade |
| Manufacturer | Exxon Chemical |
| Trade Name | Oppalyte™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | ExxonMobil Oppalyte™ 38MW247 OPP Film.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Product Description: A super white opaque biaxially oriented polypropylene film. It is designed for use in cold seal applications where superior optics and graphics are desired.Availability: Africa & Middle East, Asia Pacific and EuropeKey Features: Outstanding opacity and bright white backgroundExtra high yieldReduced show-throughHigh glossExceptional printability and receptivity to coatingsExcellent support for cold seal and high seal strengthFeatures:Light BarrierApplications: BakeryBiscuits/Cookie/Crackers Confectionery, ChocolateConfectionery, GumConfectionery, SugarCrisps and SnacksDry Foods and Beverage Powders Frozen Food Household and DetergentsIce Cream Uses:HFFS Flexible Packaging Processing Method: Cold Seal Adhesive, Inner Web Adhesive Lamination, Inner Web Extrusion Lamination, Outer Web Adhesive Lamination, Solvent Flexographic Printing, Solvent Rotogravure Printing and Surface Print UnsupportedInformation provided by ExxonMobil
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Water Vapor Transmission | 1.10 g/m²/day @Temperature 23.0 °C |
0.0710 g/100 in²/day @Temperature 73.4 °F |
85% RH; ExxonMobil Method |
| 5.28 g/m²/day @Temperature 38.0 °C |
0.340 g/100 in²/day @Temperature 100 °F |
90% RH; ExxonMobil Method | |
| Thickness | 38.1 microns | 1.50 mil | ExxonMobil Method |
| Coating Weight | 23.2 g/m² | 14.5 lb/ream | ExxonMobil Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Elongation at Break, MD | 140 % | 140 % | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
| Film Elongation at Break, TD | 50 % | 50 % | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
| Modulus of Elasticity | 1.30 GPa | 189 ksi | MD; ExxonMobil Method |
| 2.10 GPa | 305 ksi | TD; ExxonMobil Method | |
| Coefficient of Friction | 0.60 | 0.60 | Untreated Surface; ExxonMobil Method |
| Film Tensile Strength at Break, MD | 100 MPa | 14500 psi | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
| Film Tensile Strength at Break, TD | 155 MPa | 22500 psi | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Shrinkage, MD | 6.0 % @Temperature 135 °C, Time 432 sec |
6.0 % @Temperature 275 °F, Time 0.120 hour |
ExxonMobil Method |
| Shrinkage, TD | 6.0 % @Temperature 135 °C, Time 432 sec |
6.0 % @Temperature 275 °F, Time 0.120 hour |
ExxonMobil Method |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Gloss | 75 % | 75 % | 45°; ExxonMobil Method |
| Transmission, Visible | 18 % | 18 % | ExxonMobil Method |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Whiteness Index | 90 | |
| Yield | 29800 in2/lb |
Users viewing this material also viewed the following:
- Performance Polymers IPS II PPL-A1050 PEKK (Polyetherketoneketone) Branched Standard Grade
- SABIC Innovative Plastics Lexan® HPM1914 PC Copolymer
- PolyOne Edgetek® CY-1000 UV FR V0 Acrylonitrile Butadiene Styrene + PC (ABS+PC)
- Lotte Chemical Titan TITANEX® MR4086 Medium density polyethylene resin (discontinued **)
- SABIC Innovative Plastics LNP THERMOCOMP DF0049P PC
- Techmer ES Plastiblend® PA6/6 GF40 IM HS L BK 40% Glass Filled
- UBE F022SE Polyethylene
- Dow Corning 2-0400 DIMETHYLCHLOROSILANE (ME2HSICL) DIST
- Arkema Group Orgalloy® LT 4060IH Flexible Nylon Alloy (Conditioned)
- Arlon 910-10W##-P0 0.010" (0.254 mm) Cured Self-fusing Silicone Tape
Copyright © lookpolymers.com All Rights Reserved