- ExxonMobil LL 1001x74 Blown Film Resin
ExxonMobil LL 1001x74 Blown Film Resin
| Category | Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE), Film Grade |
| Manufacturer | Exxon Chemical |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | ExxonMobil LL 1001x74 Blown Film Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LL1001 are butene LLDPE blown film resins having good drawdown, tensile and toughness properties.Information provided by ExxonMobil Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.918 g/cc | 0.0332 lb/in³ | ExxonMobil Method |
| Melt Flow | 1.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
1.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| Antiblock Level | 5000 ppm | 5000 ppm | |
| Slip Level | 1700 ppm | 1700 ppm |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Tensile Strength at Yield, MD | 9.65 MPa | 1400 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 9.65 MPa | 1400 psi | ASTM D882 |
| Film Elongation at Break, MD | 580 % | 580 % | ASTM D882 |
| Film Elongation at Break, TD | 850 % | 850 % | ASTM D882 |
| Puncture Energy | 3.13 J | 2.31 ft-lb | ExxonMobil |
| Elmendorf Tear Strength, MD | 3.15 g/micron | 80.0 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 15.7 g/micron | 400 g/mil | ASTM D1922 |
| Dart Drop | 4.09 g/micron | 104 g/mil | ASTM D1709 |
| Film Tensile Strength at Break, MD | 53.1 MPa | 7700 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 35.3 MPa | 5120 psi | ASTM D882 |
| 1% Secant Modulus, MD | 193 MPa | 28000 psi | ASTM D882 |
| 1% Secant Modulus, TD | 223 MPa | 32300 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 121 °C | 249 °F | Peak Melting Temperature; ExxonMobil Method |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 15.3 % | 15.3 % | ASTM D1003 |
| Gloss | 45 % | 45 % | 45°; ASTM D2457 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Features | Thermal Stabilizer |
Users viewing this material also viewed the following:
- Proto3000 Accura® Amethyst™ Material for use with Viper™ SLA® systems
- Lord Adhesives Flocklok® 853 Blocked Flock Adhesive
- LyondellBasell Hostacomâ„¢ RTA3184 Thermoplastic Polyolefin Elastomer
- SABIC Innovative Plastics XYLEX HX8300HP PC+POLYESTER (Asia Pacific)
- Zircar Ceramics Uniform A2 Alumina-Silica Insulation
- Solvay Specialty Polymers Algoflon® E2 BP PTFE (Polytetrafluoroethylene) (discontinued **)
- Samyang Triel® 5720 Thermoplastics Polyetherester Elastomer, General Extrusion
- Spartech Spectar® UV Copolyester Sheet
Copyright © lookpolymers.com All Rights Reserved