ExxonMobil LDPE LD 302.32 Low Density Polyethylene Resin (European Grade)

Category Polymer , Thermoplastic , Polyethylene (PE) , LDPE
Manufacturer Exxon Chemical
Trade Name LDPE
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ExxonMobil LDPE LD 302.32 Low Density Polyethylene Resin (European Grade).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Product Description: LD 302 resins are 3.5% vinyl acetate copolymer, high clarity film resins. The combination of comonomer content and low melt index helps produce films which exhibit superior impact strength, good heat sealability, and good low temperature properties. Availability: Africa & Middle East, Asia Pacific and Europe Additive: Antiblock: 2500 ppmSlip: 500 ppm Thermal Stabilizer: YesInformation provided by ExxonMobil
Physical Properties Metric English Comments
Density 0.924 g/cc
0.0334 lb/in³
ExxonMobil method
Vinyl Acetate Content 3.5 %
3.5 %
ExxonMobil Method
Melt Flow 1.3 g/10 min

@Load 2.16 kg,
Temperature 190 °C
1.3 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
Antiblock Level 2500 ppm
2500 ppm
Slip Level 500 ppm
500 ppm
Mechanical Properties Metric English Comments
Film Elongation at Break, MD 190 %
190 %
ASTM D882
Film Elongation at Break, TD 580 %
580 %
ASTM D882
Elmendorf Tear Strength MD 190 g
190 g
ASTM D1922
Elmendorf Tear Strength TD 110 g
110 g
ASTM D1922
Dart Drop Test 170 g
0.375 lb
ASTM D1709A
Film Tensile Strength at Break, MD 24.1 MPa
3500 psi
ASTM D882
Film Tensile Strength at Break, TD 23.4 MPa
3400 psi
ASTM D882
1% Secant Modulus, MD 145 MPa
21000 psi
ASTM D882
1% Secant Modulus, TD 172 MPa
25000 psi
ASTM D882
Thermal Properties Metric English Comments
Melting Point <= 221 °C
<= 430 °F
Peak Melting Point; ExxonMobil method
Optical Properties Metric English Comments
Haze 6.5 %
6.5 %
ASTM D1003
Gloss 69 %
69 %
45°; ASTM D2457