ExxonMobil LD 306.75 High Clarity, High Impact Film Resin
| Category | Polymer , Film , Thermoplastic , Ethylene Vinyl Acetate , Ethylene Vinyl Acetate Copolymer (EVA), Film Grade |
| Manufacturer | Exxon Chemical |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | ExxonMobil LD 306.75 High Clarity, High Impact Film Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LD 306 Series films exhibit superior impact strength and heat sealability. Applications include food packaging and frozen food packaging.Information provided by ExxonMobil Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.924 g/cc | 0.0334 lb/in³ | ExxonMobil Method |
| Vinyl Acetate Content | 5.5 % | 5.5 % | ExxonMobil Method |
| Thickness | 38.1 microns | 1.50 mil | |
| Melt Flow | 2.0 g/10 min | 2.0 g/10 min | ExxonMobil Method |
| Antiblock Level | 3000 ppm | 3000 ppm | |
| Slip Level | 1100 ppm | 1100 ppm |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Tensile Strength at Yield, MD | 7.72 MPa | 1120 psi | at 2% offset; ASTM D882 |
| Film Tensile Strength at Yield, TD | 7.24 MPa | 1050 psi | at 2% offset; ASTM D882 |
| Film Elongation at Break, MD | 190 % | 190 % | ASTM D882 |
| Film Elongation at Break, TD | 590 % | 590 % | ASTM D882 |
| Film Elongation at Yield, MD | 7.3 % | 7.3 % | ASTM D882 |
| Film Elongation at Yield, TD | 5.9 % | 5.9 % | ASTM D882 |
| Elmendorf Tear Strength MD | 160 g | 160 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 80 g | 80 g | ASTM D1922 |
| Elmendorf Tear Strength, MD | 4.197 g/micron | 106.6 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 2.100 g/micron | 53.33 g/mil | ASTM D1922 |
| Dart Drop | 4.461 g/micron | 113.3 g/mil | ASTM D1709 |
| Dart Drop Test | 170 g | 0.375 lb | ASTM D1709 |
| Film Tensile Strength at Break, MD | 25.1 MPa | 3640 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 23.9 MPa | 3470 psi | ASTM D882 |
| 1% Secant Modulus, MD | 127 MPa | 18400 psi | ASTM D882 |
| 1% Secant Modulus, TD | 146 MPa | 21200 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 102 °C | 216 °F | Peak Melting Temperature; ExxonMobil Method |
| Crystallization Temperature | 89.0 °C | 192 °F | ExxonMobil Method |
| Vicat Softening Point | 82.8 °C | 181 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 4.0 % | 4.0 % | ASTM D1003 |
| Gloss | 74 % | 74 % | 45°; ASTM D2457 |
| Transmission, Visible | 90 % | 90 % | clear; thickness not quantified |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Features | Thermal Stabilizer |
Users viewing this material also viewed the following:
- Michelman® Hydrosize® U7-01 Polyurethane dispersion
- Saint-Gobain CHR® M832 Polyester Film Backing Silicone Adhesive Pressure Sensitive Tape
- Solvay Specialty Polymers Ryton® R-4-220NA Polyphenylene Sulfide (PPS), 40% Glass Fiber
- Ensinger NORYL® Polyphenylene oxide (PPO)
- Fainplast Compounds HGKA 79/R Flexible PVC, Sheathing for High Temperatures Lead Free
- 3M 5690K Silicone Rubber Termination Kits
- ATI Allegheny Ludlum AL 601™ Nickel-Base Alloy, Annealed at 982°C (1800°F), UNS N06601
- Mitsui AURUM® JCR3030F Thermoplastic Polyimide Resin, Wear/Friction Grade (discontinued **)
- Braskem Green PE SHC7260 Injection Molding High Density Polyethylene
Copyright © lookpolymers.com All Rights Reserved