ExxonMobil LD 117.85 Blown Overwrap Film Resin

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , LDPE , Low Density Polyethylene (LDPE), Film Grade
Manufacturer Exxon Chemical
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ExxonMobil LD 117.85 Blown Overwrap Film Resin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Product Description: LD 117.85 is a homopolymer film resin with good clarity and excellent stiffness. Film made from LD 117.85 resin can be used in overwrap applications and in push-through type packaging equipment. With narrow die gap, film produced from LD 117.85 resin can be drawn down to 1.0 mil gauge.Availability: Latin America, North America and South America Additive: Antiblock: 1000 ppmSlip: 250 ppmThermal Stabilizer: YesApplications: Bread BagsCo-Extrusion FilmsCollation ShrinkDiaper BacksheetFoamsHigh Performance Collation ShrinkHygiene PackagingLabel FilmLamination FilmOverwrap FilmPaper Overwrap Information provided by ExxonMobil Chemical
Physical Properties Metric English Comments
Density 0.929 g/cc
0.0336 lb/in³
ExxonMobil Method
Thickness 38.1 microns
1.50 mil
Melt Flow 1.6 g/10 min

@Load 2.16 kg,
Temperature 190 °C
1.6 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
Antiblock Level 1000 ppm
1000 ppm
Slip Level 250 ppm
250 ppm
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 13.8 MPa
2000 psi
ASTM D882
Film Tensile Strength at Yield, TD 15.9 MPa
2300 psi
ASTM D882
Film Elongation at Break, MD 160 %
160 %
ASTM D882
Film Elongation at Break, TD 500 %
500 %
ASTM D882
Puncture Energy 0.339 J
0.250 ft-lb
ExxonMobil Method
Elmendorf Tear Strength MD 180 g
180 g
ASTM D1922
Elmendorf Tear Strength TD 240 g
240 g
ASTM D1922
Dart Drop Test 80.0 g
0.176 lb
ASTM D1709
Film Tensile Strength at Break, MD 24.8 MPa
3600 psi
ASTM D882
Film Tensile Strength at Break, TD 17.9 MPa
2600 psi
ASTM D882
1% Secant Modulus, MD 317 MPa
46000 psi
ASTM D882
1% Secant Modulus, TD 379 MPa
55000 psi
ASTM D882
Thermal Properties Metric English Comments
Melting Point 116 °C
241 °F
Peak Melting Temperature; ExxonMobil Method
Optical Properties Metric English Comments
Haze 7.2 %
7.2 %
ASTM D1003
Gloss 68 %
68 %
45°; ASTM D2457
Descriptive Properties Value Comments
Features Thermal Stabilizer