Multibase Nylex™ 1230 Polyamide + PP
| Category | Polymer , Thermoplastic , Nylon , Polypropylene (PP) |
| Manufacturer | Multibase |
| Trade Name | Nylex™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Multibase Nylex™ 1230 Polyamide + PP.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Forms: PelletsInformation provided by Multibase
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.950 g/cc | 0.950 g/cc | ASTM 792 |
| Linear Mold Shrinkage | 0.0050 cm/cm | 0.0050 in/in | ASTM D955 |
| Melt Flow | 0.50 g/10 min @Load 2.16 kg, Temperature 230 °C |
0.50 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 20.7 MPa | 3000 psi | ASTM D638 |
| Elongation at Break | 160 % | 160 % | ASTM D638 |
| Flexural Strength | 20.7 MPa | 3000 psi | ASTM D790 |
| Flexural Modulus | 0.862 GPa | 125 ksi | Method I (3 point load), Procedure B); ASTM D790 |
| Izod Impact, Notched | 8.01 J/cm | 15.0 ft-lb/in | ASTM D256 |
| Gardner Impact | 36.16 J | 26.67 ft-lb | ASTM D3029 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 80.0 °C | 176 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 65.0 °C | 149 °F | Unannealed; ASTM D648 |
| Vicat Softening Point | 153 °C | 307 °F | ASTM D1525 |
| Flammability, UL94 | HB | HB |
Users viewing this material also viewed the following:
- SABIC F00952 High Density Polyethylene for Blown Film
- Polymer Resources PEI-G10 Polyetherimide, 10% Glass Reinforced
- PolyOne Stat-Tech™ PI-10SS/000 Polyetherimide - 10% Stainless Steel Fiber (discontinued **)
- Shinil Chemical SHINFLAME PC/ABS Flame Retardant Polymer TV Housing
- Teknor Apex Telcar® TL-2696A Thermoplastic Elastomer
- A. Schulman POLYBATCH™ White P8555 SD Concentrate Based In Homopolymer Polypropylene
- A. Schulman POLYAXIS® CP813-31 General-Purpose Polyethylene
- Dow Retain® ABS 7342 ABS
- Dow SPECTRIM™ 50-S Reaction Moldable Polymer
- Braskem TI4007G Impact Copolymer Polypropylene
Copyright © lookpolymers.com All Rights Reserved