ExxonMobil HD 6714.17 Injection Molding Resin (discontinued **)

Category	Polymer , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Injection Molded
Manufacturer
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	ExxonMobil HD 6714.17 Injection Molding Resin (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

HD 6714 is a narrow molecular weight hexene copolymer designed for outstanding processability to maximize injection molding productivity. This resin is ideally suited for thin wall multicavity parts. Lower processing temperatures enable production of products free of taste and odor for food and beverage packaging.Information provided by ExxonMobil Chemical

Physical Properties	Metric	English	Comments
Density	0.951 g/cc	0.0344 lb/in³	ASTM D4883
Environmental Stress Crack Resistance	<= 3.0 hour	<= 3.0 hour	Cond. B, 10%; ASTM D1693
Melt Flow	14 g/10 min @Load 2.16 kg, Temperature 190 °C	14 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	22.9 MPa	3320 psi	ASTM D638
Elongation at Break	61 %	61 %	ASTM D638
Flexural Modulus	0.8081 GPa	117.2 ksi	1% Secant; ASTM D790
Izod Impact, Notched	0.603 J/cm @Temperature -40.0 °C	1.13 ft-lb/in @Temperature -40.0 °F	ASTM D256
Tensile Impact Strength	332 kJ/m² @Temperature -40.0 °C	158 ft-lb/in² @Temperature -40.0 °F	ASTM D1822

Thermal Properties	Metric	English	Comments
Melting Point	131 °C	268 °F	ASTM D3418
Crystallization Temperature	114 °C	237 °F	ASTM D3418
Deflection Temperature at 0.46 MPa (66 psi)	67.0 °C	153 °F	ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	38.0 °C	100 °F	ASTM D648
Brittleness Temperature	<= -70.0 °C	<= -94.0 °F	ASTM D746

Descriptive Properties	Value	Comments
Features	Standard Processing Antioxidants Stabilizer
Form	Pellet