- Linear Low Density Polyethylene (LLDPE), Rotational Molding Grade
- ExxonMobil Escorene® LL-8361 LLDPE, Rotational Molding Powder (discontinued **)
ExxonMobil Escorene® LL-8361 LLDPE, Rotational Molding Powder (discontinued **)
| Category | Polymer , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE), Rotational Molding Grade |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | ExxonMobil Escorene® LL-8361 LLDPE, Rotational Molding Powder
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data Provided by Exxon Chemical Canada.Characteristics: Fully formulated, UV-8 type protection, Good flowUses: Consumer items, Potable water tanks, Laundry tubs
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.932 g/cc | 0.0337 lb/in³ | ASTM D4883 |
| Environmental Stress Crack Resistance | >= 500 hour | >= 500 hour | F-50; 10% Igepal Cond. B; ASTM D1693 |
| Melt Flow | 5.2 g/10 min @Load 2.16 kg, Temperature 190 °C |
5.2 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 15.9 MPa | 2310 psi | ASTM D638 |
| Elongation at Break | 765 % | 765 % | ASTM D638 |
| Flexural Modulus | 0.503 GPa | 73.0 ksi | ASTM D790 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 125 °C | 257 °F | Exxon Method |
| Deflection Temperature at 0.46 MPa (66 psi) | 49.0 °C | 120 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 37.0 °C | 98.6 °F | ASTM D648 |
Users viewing this material also viewed the following:
- Plenco 5314 Black (INJ) Impact Grade Phenolic Molding Compound (discontinued **)
- Techmer ES HiFill FR® PC FR SFX-ORANGE 1.0
- Samyang Trirex® PC-3025IR 10 MFI Clear Polycarbonate With Release
- SABIC Innovative Plastics LNP STAT-KON RE007 PA 66
- Styrolution Terblend® N NG-02 8% Glass Filled ABS/PA6 (Dry)
- A. Schulman POLYBATCH™ White LL8000 AP Concentrate Based In LLDPE
- CENTROPLAST BC NF Organic Thermoplastic, 15% Natural Fiber
- Arkema Group KYNAR® 740 Polyvinylidene Fluoride Homopolymer - Injection Molding and Extrusion
- Haynes 625 alloy, 40% cold reduction
Copyright © lookpolymers.com All Rights Reserved