SABIC Innovative Plastics NORYL GTX GTX909 PPE+PS+PA (Asia Pacific)
| Category | Polymer , Thermoplastic , Nylon , Polyphenylene Ether/PPO , Polystyrene (PS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | NORYL GTX |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics NORYL GTX GTX909 PPE+PS+PA (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
400F (205C) HDT. 3.3 Notched Izod. Excellent chemical resistance
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.13 g/cc | 1.13 g/cc | ASTM D792 |
| Water Absorption | 0.54 % @Time 86400 sec |
0.54 % @Time 24.0 hour |
ASTM D570 |
| Moisture Absorption at Equilibrium | 4.4 % | 4.4 % | ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.013 - 0.017 cm/cm @Thickness 3.20 mm |
0.013 - 0.017 in/in @Thickness 0.126 in |
SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 59.0 MPa | 8560 psi | Type I, 50 mm/min; ASTM D638 |
| Tensile Strength, Yield | 66.0 MPa | 9570 psi | Type I, 50 mm/min; ASTM D638 |
| Elongation at Break | 50 % | 50 % | Type I, 50 mm/min; ASTM D638 |
| Elongation at Yield | 9.0 % | 9.0 % | Type I, 50 mm/min; ASTM D638 |
| Flexural Yield Strength | 99.0 MPa | 14400 psi | 2.6 mm/min, 100 mm span; ASTM D790 |
| Flexural Modulus | 2.37 GPa | 344 ksi | 2.6 mm/min, 100 mm span; ASTM D790 |
| Izod Impact, Notched | 1.76 J/cm | 3.30 ft-lb/in | ASTM D256 |
| 1.06 J/cm @Temperature -30.0 °C |
1.99 ft-lb/in @Temperature -22.0 °F |
ASTM D256 | |
| Dart Drop, Total Energy | 40.0 J | 29.5 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| 24.0 J @Temperature -30.0 °C |
17.7 ft-lb @Temperature -22.0 °F |
Instrumented Impact Energy @ peak; ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 95.4 µm/m-°C @Temperature -20.0 - 150 °C |
53.0 µin/in-°F @Temperature -4.00 - 302 °F |
ASTM E 831 |
| CTE, linear, Transverse to Flow | 81.0 µm/m-°C @Temperature -20.0 - 150 °C |
45.0 µin/in-°F @Temperature -4.00 - 302 °F |
ASTM E 831 |
| Deflection Temperature at 0.46 MPa (66 psi) | 204 °C @Thickness 6.40 mm |
399 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 125 °C @Thickness 6.40 mm |
257 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| Vicat Softening Point | 245 °C | 473 °F | Rate B/50; ASTM D1525 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 4.40e+16 ohm-cm | 4.40e+16 ohm-cm | ASTM D257 |
| Surface Resistance | 1.70e+16 ohm | 1.70e+16 ohm | ASTM D257 |
| Dielectric Constant | 2.76 @Frequency 1.00e+6 Hz |
2.76 @Frequency 1.00e+6 Hz |
ASTM D150 |
| 3.27 @Frequency 50.0 - 60.0 Hz |
3.27 @Frequency 50.0 - 60.0 Hz |
ASTM D150 | |
| Dielectric Strength | 25.5 kV/mm @Thickness 3.20 mm |
648 kV/in @Thickness 0.126 in |
in oil; ASTM D149 |
| Dissipation Factor | 0.019 @Frequency 1.00e+6 Hz |
0.019 @Frequency 1.00e+6 Hz |
ASTM D150 |
| 0.039 @Frequency 50.0 - 60.0 Hz |
0.039 @Frequency 50.0 - 60.0 Hz |
ASTM D150 |
Users viewing this material also viewed the following:
- Lanxess Durethan® BKV 30 H3.0 000000 Nylon 6, 30% Glass Fiber
- Karina 40/272-FC-LMP Green Color Concentrate for PVC
- ChevronTexaco 17 MG 2000 Diesel Engine Oil
- EMS-Grivory Grivory® XE 4217 black 9233 PA6T/66-GF45
- Arlon 19571R025 0.025" (0.635 mm) Uncured Silicone Rubber with Fiberglass Substrate
- Amity Thermosets ATM 123 Phenolic Molding Organic Filler, Compression Molded
- Bostik 6370 Very Flexible EVA Glue Stick
- Toyobo E3070A Thermoplastic Polyurethane Elastomer, Extrusion Grade
- Gromax CFG33-QS11N1 Nylon 6 33% Glass Filled (Dry)
Copyright © lookpolymers.com All Rights Reserved