ExxonMobil Escorene® LD 713.93 Molding, extrusion and compounding resin

Category Polymer , Thermoplastic , Ethylene Vinyl Acetate , Ethylene Vinyl Acetate Copolymer (EVA), Extrusion/Coating Grade
Manufacturer Exxon Chemical
Trade Name Escorene®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ExxonMobil Escorene® LD 713.93 Molding, extrusion and compounding resin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Escorene Ultra LD 713.93 is a 14.4 wt% vinyl acetate copolymer with very good toughness, high clarity and excellent processability. It is suitable for use in making molded articles, extruded profiles and compounds.Availability: Latin America, North America and South America Additive: Thermal Stabilizer: Yes Applications:CompoundingFlexible HosesProfile ExtrusionTube ExtrusionInformation provided by ExxonMobil Chemical
Physical Properties Metric English Comments
Density 0.933 g/cc
0.0337 lb/in³
ExxonMobil Method
Vinyl Acetate Content 14.4 %
14.4 %
ExxonMobil Method
Melt Flow 3.50 g/10 min

@Load 2.16 kg,
Temperature 190 °C
3.50 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Shore A 83
83
15s; ASTM D2240
Hardness, Shore D 33
33
15s; ASTM D2240
Tensile Strength at Break 10.3 MPa
1500 psi
ASTM D638
Tensile Strength, Yield 5.52 MPa
800 psi
ASTM D638
Elongation at Break 750 %
750 %
ASTM D638
Elongation at Yield 170 %
170 %
ASTM D638
Flexural Modulus 0.0600 GPa
8.70 ksi
1% secant; ASTM D790
Impact Test 14.9 J

@Temperature 23.0 °C
11.0 ft-lb

@Temperature 73.4 °F
Instrument Impact, Total Energy; ASTM D3763
29.8 J

@Temperature -40.0 °C
22.0 ft-lb

@Temperature -40.0 °F
Instrumented Impact, Total Energy; ASTM D3763
Thermal Properties Metric English Comments
Melting Point 87.8 °C
190 °F
Peak Melting Temperature; ExxonMobil Method
Vicat Softening Point 62.8 °C
145 °F
ASTM D1525
Copyright © lookpolymers.com All Rights Reserved