ExxonMobil Escorene™ FL 00212 Ethylene Vinyl Acetate Copolymer (European Grade)

Category	Polymer , Thermoplastic , Ethylene Vinyl Acetate
Manufacturer	Exxon Chemical
Trade Name	Escorene™
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	ExxonMobil Escorene™ FL 00212 Ethylene Vinyl Acetate Copolymer (European Grade).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Product Description: FL 00212 is a copolymer of ethylene and vinyl acetate. Processing Conditions: Processing temperatures above 260°C (500°F) may cause resin degradation. Machines should always be purged with LDPE or suitable cleaning compound before shutdown.Availability: Africa & Middle East and Europe Additive: Antiblock: NoSlip: NoThermal Stabilizer: Yes Applications:Cast FilmCo-Extrusion FilmsCompoundingFreezer FilmInjection MoldingStretch FilmInformation provided by ExxonMobil

Physical Properties	Metric	English	Comments
Density	0.933 g/cc	0.0337 lb/in³	ExxonMobil method
Vinyl Acetate Content	12 %	12 %	ExxonMobil method
Melt Flow	2.5 g/10 min @Load 2.16 kg, Temperature 190 °C	2.5 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	92 @Time 15.0 sec	92 @Time 0.00417 hour	Molded Properties; ISO 868
Tensile Strength at Break	>= 0.689 MPa	>= 100 psi	Molded Properties; ISO 527-2/1A
Film Elongation at Break, MD	600 %	600 %	ASTM D882
Film Elongation at Break, TD	650 %	650 %	ASTM D882
Tensile Modulus	0.0689 GPa	10.0 ksi	Molded Properties; ISO 527-2/1
Elmendorf Tear Strength MD	130 g	130 g	ASTM D1922
Elmendorf Tear Strength TD	190 g	190 g	ASTM D1922
Dart Drop Test	510 g	1.12 lb	ASTM D1709A
Film Tensile Strength at Break, MD	30.3 MPa	4400 psi	ASTM D882
Film Tensile Strength at Break, TD	28.3 MPa	4100 psi	ASTM D882
1% Secant Modulus, MD	68.9 MPa	10000 psi	ASTM D882
1% Secant Modulus, TD	68.9 MPa	10000 psi	ASTM D882

Thermal Properties	Metric	English	Comments
Melting Point	<= 199 °C	<= 390 °F	Peak Melting Point; ExxonMobil method
Vicat Softening Point	72.2 °C	162 °F	ASTM D1525

Descriptive Properties	Value	Comments
Blending Temperature	260