ExxonMobil Bicor™ 29MB080 OPP Film
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Film Grade |
| Manufacturer | Exxon Chemical |
| Trade Name | Bicor™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | ExxonMobil Bicor™ 29MB080 OPP Film.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Product Description: A biaxially oriented polypropylene film metallizable on one side, with a heat sealable surface on the other side. Designed to be used after metallization as a single web in HFFS applications or in laminations for other purposes.Availability: Africa & Middle East, Asia Pacific and EuropeKey Features:Good adhesion layer for metallizationExcellent processability in metallizationGood machinability on HFFS machineVery good hot tackOne side sealableHigh yieldBrilliant metal appearance after metallizationFeatures: In Lamination Lap SealableApplications:Industrial Uses: HFFS Flexible PackagingInformation provided by ExxonMobil
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Water Vapor Transmission | 1.01 g/m²/day @Temperature 23.0 °C |
0.0650 g/100 in²/day @Temperature 73.4 °F |
85% RH; ExxonMobil Method |
| 4.50 g/m²/day @Temperature 38.0 °C |
0.290 g/100 in²/day @Temperature 100 °F |
90% RH; ExxonMobil Method | |
| Thickness | 27.9 microns | 1.10 mil | ExxonMobil Method |
| Coating Weight | 25.9 g/m² | 16.2 lb/ream | ExxonMobil Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Elongation at Break, MD | 175 % | 175 % | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
| Film Elongation at Break, TD | 60 % | 60 % | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
| Modulus of Elasticity | 2.00 GPa | 290 ksi | MD; ExxonMobil Method |
| 3.60 GPa | 522 ksi | TD; ExxonMobil Method | |
| Coefficient of Friction | 0.65 | 0.65 | Treated Surface; ExxonMobil Method |
| 0.65 | 0.65 | Untreated Surface; ExxonMobil Method | |
| Seal Strength | 460 g/25 mm @Pressure 0.276 MPa, Temperature 140 °C |
460 g/in @Pressure 40.0 psi, Temperature 284 °F |
Otto Brugger, 0.2 sec; ExxonMobil Method |
| Film Tensile Strength at Break, MD | 150 MPa | 21800 psi | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
| Film Tensile Strength at Break, TD | 290 MPa | 42100 psi | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Shrinkage, MD | 6.5 % @Temperature 135 °C, Time 432 sec |
6.5 % @Temperature 275 °F, Time 0.120 hour |
ExxonMobil Method |
| Shrinkage, TD | 4.5 % @Temperature 135 °C, Time 432 sec |
4.5 % @Temperature 275 °F, Time 0.120 hour |
ExxonMobil Method |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 2.0 % | 2.0 % | ExxonMobil Method |
| Gloss | 85 % | 85 % | 45°; ExxonMobil Method |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Heat Seal Range | 54°F | 36.3 psi, 0.2 sec |
| Yield | 26600 in2/lb |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® FXM1413T PC Copolymer (Europe-Africa-Middle East)
- DuPont Bynel® 4003 Anhydride-Modified HDPE Adhesive Resin (discontinued **)
- Kennametal Stellite Stellite® 31 PM with P/M Processing; heat treated at 93°C (200°F) and water quenched
- Manifattura Cattaneo RULON® 641 Polytetrafluoroethylene
- Karina E 856-08/151-Y-ERYB Beige PVC Compound
- SABIC Innovative Plastics LNP LUBRICOMP KL001 Acetal Copolymer
- Skamol Group V-1100 600 Vermiculite Insulating Slab
- A. Schulman POLYBATCH™ Blue LL40299U/3 Concentrate Based In LLDPE
- Azdel Plus C321B02N 32% Chopped Fiber Mat / PP Resin Matrix
- 3M Scotch-Weld™ 2214 Hi-Temp New Formula Epoxy Adhesive
Copyright © lookpolymers.com All Rights Reserved