ExxonMobil Bicor® 100 SLP OPP Film
| Category | Polymer , Film , Thermoplastic , Polypropylene (PP) , Polypropylene, Film Grade |
| Manufacturer | Exxon Chemical |
| Trade Name | Bicor® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | ExxonMobil Bicor® 100 SLP OPP Film.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Product Description: Bicor SLP is a one-side treated, non-heat sealable OPP film designed for use as the outside web of a lamination. The treated print surface is intended as the print and laminating side.Availability: Latin America, North America and South AmericaKey Features:Excellent ink adhesion and bond strength in adhesive, PVdC adhesive, and extrusion laminationsNon-migratory slip system for consistent COFApplications:BakeryBiscuits/Cookie/Crackers Confectionery, Gum Confectionery, SugarCrisps and SnacksFresh Produce Uses:HFFS Flexible PackagingPouches – Flexible Packaging VFFS Flexible PackagingProcessing Method: Outer Web Adhesive Lamination, Outer Web Extrusion Lamination, Solvent Flexographic Printing, Solvent Rotogravure Printing and Water-based Flexographic PrintingInformation provided by ExxonMobil Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Water Vapor Transmission | 5.10 g/m²/day | 0.328 g/100 in²/day | 38°C, 90% RH; ExxonMobil Method |
| Thickness | 25.4 microns | 1.00 mil | Nominal; ExxonMobil Method |
| Coating Weight | 22.7 g/m² | 14.2 lb/ream | ExxonMobil Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Coefficient of Friction | 0.20 | 0.20 | slip modified; ExxonMobil Method |
| Film Tensile Strength at Break, MD | 124 MPa | 18000 psi | 20 in/min, 2.0 in Jaw Separation; ExxonMobil Method |
| Film Tensile Strength at Break, TD | 241 MPa | 35000 psi | 20 in/min, 2.0 in Jaw Separation; ExxonMobil Method |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Shrinkage, MD | 4.0 % | 4.0 % | at 275°F; ExxonMobil Method |
| Shrinkage, TD | 4.0 % | 4.0 % | at 275°F; ExxonMobil Method |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 2.0 % | 2.0 % | ExxonMobil Method |
| Gloss | 87 % | 87 % | 45°, Untreated Surface; ExxonMobil Method |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Wetting Tension | 0.83 receding COS theta | Print Surface |
| Yield | 30500 in2/lb |
Users viewing this material also viewed the following:
- Plastcom SLOVAMID 6 GF 15 T 25 TS PA6, 15% glass fibre, 25% mineral filling
- Nylene® 9110 G33 , 33% Glass Reinforced Nylon 6/10
- PolyOne Edgetek® AS-50GF/000 Acrylonitrile Butadiene Styrene (ABS), Glass Filled (discontinued **)
- Hexcel® HexWeb® HRH-10 - 3/4 - 1.5 Aramid Fiber/Phenolic Resin Honeycomb
- Arlon EP2 Enhanced Polyimide Laminate and Prepreg
- BASF Ultraform® W2320 0035 POM
- Overview of materials for Acetal Copolymer, PTFE Filled
- PolyOne Edgetek® MLS-XC195C-2 Polysulfone Alloy - ESD Material - Lubricated (discontinued **)
Copyright © lookpolymers.com All Rights Reserved