Eurostar Staramide 6 70E3 PA6, 70% Mineral Filled, Injection Molded
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 |
| Manufacturer | Eurostar Engineering Plastics |
| Trade Name | Staramide |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Eurostar Staramide 6 70E3 PA6, 70% Mineral Filled, Injection Molded.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Staramide 6 70E3 is a 70% mineral filled high density, Polyamide 6 Injection Molding ResinInformation provided by Eurostar.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 2.30 g/cc | 0.0831 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.011 - 0.014 cm/cm @Thickness 4.00 mm |
0.011 - 0.014 in/in @Thickness 0.157 in |
E2P method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 77.0 MPa | 11200 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 1.3 % | 1.3 % | 5 mm/min; ISO 527 |
| Flexural Strength | 103 MPa | 14900 psi | ISO 178 |
| Flexural Modulus | 6.80 GPa | 986 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 3.10 kJ/m² | 1.48 ft-lb/in² | 80x10x4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 18.0 kJ/m² | 8.57 ft-lb/in² | 80x10x4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 123 °C | 253 °F | Flatw 80x10x4, sp=64 mm; ISO 75/Af |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Zone 1 | 250 - 260 °C | 482 - 500 °F | |
| Zone 2 | 265 - 275 °C | 509 - 527 °F | |
| Melt Temperature | 265 - 275 °C | 509 - 527 °F | |
| Mold Temperature | 80.0 - 95.0 °C | 176 - 203 °F | |
| Drying Temperature | 80.0 °C @Time 14400 sec |
176 °F @Time 4.00 hour |
|
| Moisture Content | 0.20 % | 0.20 % |
Users viewing this material also viewed the following:
- Rotuba 856, Slow Burning Ethyl Cellulose
- SABIC Innovative Plastics Lexan® ML3513 PC (Europe-Africa-Middle East)
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 75 PHR Atomite Whiting Filler
- Meehanite AQ Flake Graphite Cast Iron
- SABIC Innovative Plastics LNP LUBRICOMP KFP032 Acetal Copolymer
- SABIC Innovative Plastics LNP THERMOCOMP RF002XXH PA 66
- Crucible Steel Aquamet® 17 Martensitic Steel
- Arlon 0.029" (0.7366 mm) Flexible Heater Silicone with Fiberglass Substrate (55589R028)
- Addiplast Addinyl B2 V40 Nylon 6, 40% Glass Filled
Copyright © lookpolymers.com All Rights Reserved