Ecomass® 1850ZN66T1 Steel Powder Filled Polyamide, Injection Molding

Category	Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Impact Grade
Manufacturer	Ecomass Technologies
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Ecomass® 1850ZN66T1 Steel Powder Filled Polyamide, Injection Molding.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Steel Powder Filled Polyamide (PA6), Impact Modified, Product Form - PelletsProcessing Method: Injection MoldingNontoxic alternative to Lead, weighting and balancing applicationsInformation provided by Technical Polymers.

Physical Properties	Metric	English	Comments
Specific Gravity	2.50 g/cc	2.50 g/cc	Internal Method
Linear Mold Shrinkage	0.0080 - 0.010 cm/cm	0.0080 - 0.010 in/in

Mechanical Properties	Metric	English	Comments
Tensile Strength	31.0 MPa	4500 psi	ISO 527
Elongation at Break	10 %	10 %	ISO 527
Flexural Modulus	2.80 GPa	406 ksi	ISO 178

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	150 °C	302 °F	ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	50.0 °C	122 °F	ASTM D648

Processing Properties	Metric	English	Comments
Melt Temperature	230 - 260 °C	446 - 500 °F
Mold Temperature	65.0 - 80.0 °C	149 - 176 °F
Drying Temperature	80.0 °C	176 °F
Dry Time	4 - 6 hour	4 - 6 hour
Moisture Content	<= 0.20 %	<= 0.20 %	target