Eastman Tenite Acetate 109E3V46022 Natural, Trsp Cellulose Acetate (discontinued **)

Category	Polymer , Renewable/Recycled Polymer , Thermoplastic , Cellulosic , Cellulose Acetate, Molded
Manufacturer
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Eastman Tenite Acetate 109E3V46022 Natural, Trsp Cellulose Acetate (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Plasticizer 25%. Weight loss on heating = 1.2% per ASTM D 707. Soluble matter loss = 0.2% per ASTM D 570.Product Description: TENITE cellulosic plastics are noted for their excellent balance of properties - toughness, hardness, strength, surface gloss, clarity, and a warm feel. The mechanical properties of TENITE cellulosic plastics differ with plasticizer levels. Lower plasticizer content yields a harder surface, higher heat resistance, greater rigidity, higher tensile strength, and better dimensional stability. Higher plasticizer content increases impact strength. TENITE cellulosic plastics are available in natural, clear, amber, and black. Color concentrates are available in let-down ratios from 10:1 to 40:1. TENITE Cellulose Acetate 109-22 has a plasticizer level of 22%. Applications: OphthalmicTechnical Data Sheet Comments: Properties reported here are typical of average lots. Eastman makes no representation that the material in any particular shipment will conform exactly to the values giveInformation provided by Eastman Chemical.

Physical Properties	Metric	English	Comments
Density	1.28 g/cc	0.0462 lb/in³	ASTM D792
Water Absorption	2.3 %	2.3 %	24 hour immersion; ASTM D570
Linear Mold Shrinkage	0.0040 cm/cm	0.0040 in/in	ASTM D955

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	90	90	ASTM D785
Tensile Strength, Ultimate	40.7 MPa	5900 psi	ASTM D638
Tensile Strength, Yield	37.2 MPa	5400 psi	ASTM D638
Elongation at Break	25 %	25 %	ASTM D638
Flexural Yield Strength	62.7 MPa	9090 psi	ASTM D790
Flexural Modulus	2.344 GPa	340.0 ksi	ASTM D790
Izod Impact, Notched	1.60 J/cm	3.00 ft-lb/in	ASTM D256
	0.480 J/cm @Temperature -40.0 °C	0.899 ft-lb/in @Temperature -40.0 °F	ASTM D256

Thermal Properties	Metric	English	Comments
CTE, linear	11.0 - 17.0 µm/m-°C @Temperature 20.0 °C	6.11 - 9.44 µin/in-°F @Temperature 68.0 °F	ASTM D696
Specific Heat Capacity	1.465 J/g-°C	0.3501 BTU/lb-°F	DSC
Thermal Conductivity	0.250 W/m-K	1.74 BTU-in/hr-ft²-°F	ASTM C177
Deflection Temperature at 0.46 MPa (66 psi)	86.0 °C	187 °F	ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	77.0 °C	171 °F	Conditioned 4 hours @ 70°C (158°F); ASTM D648
Vicat Softening Point	113 °C	235 °F	Conditioned 4 hours @ 70°C (158°F); ASTM D1525

Optical Properties	Metric	English	Comments
Refractive Index	1.475	1.475	ASTM D542
Haze	<= 8.5 % @Thickness 1.52 mm	<= 8.5 % @Thickness 0.0598 in	ASTM D1003
Transmission, Visible	>= 90 % @Thickness 1.52 mm	>= 90 % @Thickness 0.0598 in	ASTM E308

Electrical Properties	Metric	English	Comments
Electrical Resistivity	1.00e+13 - 1.00e+15 ohm-cm	1.00e+13 - 1.00e+15 ohm-cm	ASTM D257
Dielectric Constant	3.55 @Frequency 1e+6 Hz	3.55 @Frequency 1e+6 Hz	ASTM D 150
Dielectric Strength	15.25 kV/mm	387.4 kV/in	ASTM D149
Dissipation Factor	0.080 @Frequency 1e+6 Hz	0.080 @Frequency 1e+6 Hz	ASTM D150