Eastman Tenite 358-15 CAP Cellulose Acetate Propionate (discontinued **)
| Category | Polymer , Renewable/Recycled Polymer , Thermoplastic , Cellulosic , Cellulose Acetate Propionate, Molded |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Eastman Tenite 358-15 CAP Cellulose Acetate Propionate
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
15% Plasticized. ISO data as provided by the manufacturer, Eastman Chemical.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.19 g/cc | 0.0430 lb/in³ | |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0060 cm/cm @Thickness 3.20 mm |
0.0020 - 0.0060 in/in @Thickness 0.126 in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 28.0 MPa | 4060 psi | 50 mm/min |
| Elongation at Break | 34 % | 34 % | |
| Elongation at Yield | 3.7 % | 3.7 % | |
| Tensile Modulus | 1.41 GPa | 205 ksi | 1mm/min |
| Charpy Impact Unnotched | NB | NB | |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
||
| Charpy Impact, Notched | 2.61 J/cm² | 12.4 ft-lb/in² | |
| 0.720 J/cm² @Temperature -30.0 °C |
3.43 ft-lb/in² @Temperature -22.0 °F |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 112 µm/m-°C @Temperature 20.0 °C |
62.2 µin/in-°F @Temperature 68.0 °F |
|
| CTE, linear, Transverse to Flow | 133 µm/m-°C @Temperature 20.0 °C |
73.9 µin/in-°F @Temperature 68.0 °F |
|
| Deflection Temperature at 0.46 MPa (66 psi) | 86.0 °C | 187 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 77.0 °C | 171 °F | |
| Vicat Softening Point | 81.0 °C | 178 °F | |
| Glass Transition Temp, Tg | 90.0 °C | 194 °F |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 210 - 220 °C | 410 - 428 °F |
Users viewing this material also viewed the following:
- Oxford Polymers 40GF 40% Glass Fiber Reinforced Polyphenylene Sulfide
- Polymer Resources TP-FR IM PBT, Impact Modified, Flame Retardant, Low Flow
- KB Alloys 10% Strontium Aluminum Waffle Ingot, Rod | Buttons, Korrect Bar
- M Chemical GUARD DOGâ„¢ UV234 Light Absorber, Benzotriazole Derivative
- KaMin KaMin® 2000C Kaolin Clay - Calcined
- Teknor Apex APEX® 4167 Polyvinyl Chloride, Flexible
- Solvay MACKADET® CA-ND Surfactant
- Loctite® PST® 565 Thread Sealant
- Aptek 2209-A/B Clear, non-yellowing urethane adhesive
Copyright © lookpolymers.com All Rights Reserved