SPS Guang Zhou SAMATâ„¢ 666(f1) Flame-retarded Polypropylene
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Flame Retardant |
| Manufacturer | SPS Guang Zhou |
| Trade Name | SAMAT™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SPS Guang Zhou SAMATâ„¢ 666(f1) Flame-retarded Polypropylene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Characteristic: Flame retardance, weather resistance, good mechanical propertiesApplications: X'mas decorative product, E/E applianceInformation Provided by SPS (Guang Zhou) Ltd.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.20 g/cc | 1.20 g/cc | ASTM D792 |
| Melt Flow | 9.0 g/10 min | 9.0 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 20.0 MPa | 2900 psi | ASTM D638 |
| Flexural Strength | 30.0 MPa | 4350 psi | |
| Flexural Modulus | 1.30 GPa | 189 ksi | |
| Izod Impact, Notched | 0.360 J/cm | 0.674 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 110 °C | 230 °F | ASTM D648 |
| Flammability, UL94 | V-0 | V-0 |
Users viewing this material also viewed the following:
- Nylene® 600 Nylon 6, 50% RH, Extrusion Grade
- LG Chemical Lupox® GP-2151F General Purpose PBT, 15% Glass Fiber Reinforced, Flame Retardant
- SABIC Innovative Plastics LNP THERMOCOMP UFW49RSC PPA (Europe-Africa-Middle East)
- A. Schulman POLYFORT™ PP 3052UX Impact Resistant Copolymer
- Goodfellow Platinum 90/Iridium 10 Alloy
- DuPont™ Surlyn® 8150 Ionomer Resin, Sodium
- CMW® ELKONIUM 30 pure platinum
- Aptek 2313-PMF Hybrid Epoxy Adhesive
- DuPont Performance Polymers VTR 8710 (ETP-600S) Peroxide Cured Fluoroelastomer (FKM) Formulation (discontinue
Copyright © lookpolymers.com All Rights Reserved