Eastman Eastar 6763 PETG Copolyester
| Category | Polymer , Thermoplastic , Polyester, TP , Polyethylene Terephthalate (PET) |
| Manufacturer | Eastman Chemical |
| Trade Name | Eastar |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Eastman Eastar 6763 PETG Copolyester.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
ISO data as provided by the manufacturer, Eastman Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.27 g/cc | 0.0459 lb/in³ | |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0050 cm/cm | 0.0020 - 0.0050 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 48.0 MPa | 6960 psi | 50 mm/min |
| Elongation at Break | >= 50 % | >= 50 % | |
| Elongation at Yield | 4.2 % | 4.2 % | |
| Tensile Modulus | 2.09 GPa | 303 ksi | 1mm/min |
| Charpy Impact Unnotched | NB | NB | |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
||
| Charpy Impact, Notched | 0.670 J/cm² | 3.19 ft-lb/in² | |
| 0.420 J/cm² @Temperature -30.0 °C |
2.00 ft-lb/in² @Temperature -22.0 °F |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 77.0 µm/m-°C @Temperature 20.0 °C |
42.8 µin/in-°F @Temperature 68.0 °F |
|
| CTE, linear, Transverse to Flow | 83.0 µm/m-°C @Temperature 20.0 °C |
46.1 µin/in-°F @Temperature 68.0 °F |
|
| Specific Heat Capacity | 1.30 J/g-°C | 0.311 BTU/lb-°F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 70.0 °C | 158 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 66.0 °C | 151 °F | |
| Vicat Softening Point | 74.0 °C | 165 °F | |
| Glass Transition Temp, Tg | 81.0 °C | 178 °F | |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|
| HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
||
| V-2 @Thickness 3.20 mm |
V-2 @Thickness 0.126 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | |
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | |
| Dielectric Strength | 16.0 kV/mm | 406 kV/in | |
| Dissipation Factor | 0.020 @Frequency 1e+6 Hz |
0.020 @Frequency 1e+6 Hz |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 250 - 270 °C | 482 - 518 °F |
Users viewing this material also viewed the following:
- Neutrex Purgex™ 3057 Plus Purging Compound
- Solvay Specialty Polymers Hylar® 460 PVDF Polyvinylidene Fluoride (discontinued **)
- Huntsman IROGRAN® A 85 E 5719 FCM TPU-Polyester
- Solvay Specialty Polymers Ryton® BR111BL Polyphenylene Sulfide (PPS), GlassMineral Filled
- SABIC Innovative Plastics Valox® 855 PBT (Asia Pacific)
- Schmelzer Industries Pearlveil 110-20 Fiberglass Veil
- Borealis BEC5012 Polypropylene Block Copolymer for Non-Pressure Pipes
- A. Schulman PP 3457-01 Copolymer Polypropylene
- Zircar Ceramics AS-1260 Alumina-Silica Textile
Copyright © lookpolymers.com All Rights Reserved