- Polykemi AB SCANTEC PC S75R GF20 Polycarbonate, Glass Fiber Reinforced
Polykemi AB SCANTEC PC S75R GF20 Polycarbonate, Glass Fiber Reinforced
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, 20% Glass Filled |
| Manufacturer | Polykemi AB |
| Trade Name | SCANTEC |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polykemi AB SCANTEC PC S75R GF20 Polycarbonate, Glass Fiber Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Polykemi AB
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.35 g/cc | 0.0488 lb/in³ | ISO 1183 |
| Filler Content | 20 % | 20 % | ±2%; Polykemi |
| Linear Mold Shrinkage | 0.0020 cm/cm | 0.0020 in/in | With Flow; ISO 2577 |
| 0.0050 cm/cm | 0.0050 in/in | Across Flow; ISO 2577 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | <= 80.0 MPa | <= 11600 psi | ISO/R527 |
| Elongation at Break | 2.0 % | 2.0 % | ISO/R527 |
| Flexural Strength | <= 145 MPa | <= 21000 psi | ISO 178 |
| Flexural Modulus | 5.50 GPa @Temperature 23.0 °C |
798 ksi @Temperature 73.4 °F |
ISO 178 |
| Charpy Impact, Notched | 0.600 J/cm² @Temperature -20.0 °C |
2.86 ft-lb/in² @Temperature -4.00 °F |
ISO 179 |
| 0.800 J/cm² @Temperature 23.0 °C |
3.81 ft-lb/in² @Temperature 73.4 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 140 °C | 284 °F | 120°C/h; ISO 75/1 |
| Deflection Temperature at 1.8 MPa (264 psi) | 135 °C | 275 °F | 120°C/h; ISO 75/1 |
| Vicat Softening Point | 147 °C @Load 5.001 kg |
297 °F @Load 11.03 lb |
50°C/h; ISO 306 |
| Flammability, UL94 | V-2 @Thickness 1.60 mm |
V-2 @Thickness 0.0630 in |
|
| Glow Wire Test | 960 °C @Thickness 3.20 mm |
1760 °F @Thickness 0.126 in |
IEC 695-2-1 |
Users viewing this material also viewed the following:
- Premix Thermoplastics PREBLACK PP 704-35 Polypropylene, 35% Carbon Black
- Haynes Hastelloy® S alloy, gas tungsten arc welded plate 12.7 mm (1/2 in.) thick, aged 16000 hours
- Spartech Polycast Cell Cast Acrylic
- Special Metals FERRY® Alloy
- Shin-Etsu Silicones KSP-100 Fluid
- Total MDPE LF 38 YS CF Medium Density Polyethylene, Stripes
- A. Schulman POLYFORT™ FPP 1220 Glass Filled Chemically Coupled Impact Copolymer Polypropylene
- A. Schulman SCHULAMID® 66 GF40H 40% Glass Fiber Reinforced, Heat Stabilized Nylon 66