EPICHEM PA 66 GF 30 Polyamide 66, 30% Glass
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled |
| Manufacturer | EPICHEM srl |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | EPICHEM PA 66 GF 30 Polyamide 66, 30% Glass.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Characteristics: 30% glass fibre filled
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.36 g/cc | 0.0491 lb/in³ | ASTM D792, ISO 1183 |
| Water Absorption | 6.0 % @Temperature 23.0 °C |
6.0 % @Temperature 73.4 °F |
24h; ASTM D570, ISO 62 |
| Linear Mold Shrinkage | 0.0020 - 0.011 cm/cm | 0.0020 - 0.011 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell L | 110 | 110 | ASTM D785, ISO 2039/2 |
| Tensile Strength, Yield | 150 MPa | 21800 psi | ASTM D638, ISO R527 |
| Elongation at Break | 2.5 % | 2.5 % | ASTM D638, ISO R527 |
| Flexural Strength | 210 MPa | 30500 psi | ASTM D790, ISO 178 |
| Flexural Modulus | 8.00 GPa | 1160 ksi | ASTM D790, ISO 178 |
| Izod Impact, Notched | 0.600 - 0.800 J/cm @Thickness 3.20 mm, Temperature 23.0 °C |
1.12 - 1.50 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F |
ASTM D256, ISO 180/4a |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 90.0 °C | 194 °F | 20000 h; VDE 0304/P2-1, IEC 216 |
| 100 °C | 212 °F | 5000 h; VDE 0304/P2-1, IEC 216 | |
| 200 °C | 392 °F | few hours; VDE 0304/P2-1, IEC 216 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 180 °C | 356 °F | ASTM D648, ISO 75 |
| Vicat Softening Point | 240 °C @Load 5.00 kg |
464 °F @Load 11.0 lb |
120°C/min; ASTM D1525/B, ISO 306/B |
| 245 °C @Load 0.999 kg |
473 °F @Load 2.20 lb |
120°C/min; ASTM D1525/A, ISO 306/A | |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|
| HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | ASTM D257, IEC 93 |
| Dielectric Constant | 3.5 @Frequency 1000 Hz |
3.5 @Frequency 1000 Hz |
ASTM D150, IEC 250 |
| Dielectric Strength | 80.0 kV/mm | 2030 kV/in | ASTM D149, IEC 243 |
| Dissipation Factor | 0.020 @Frequency 1000 Hz |
0.020 @Frequency 1000 Hz |
ASTM D150, IEC 250 |
| Comparative Tracking Index | 425 V | 425 V | VDE 0303-P1, IEC 112 |
Users viewing this material also viewed the following:
- Lanxess Durethan® DP 2802/30 000000 Nylon 66, 30% Glass Fiber
- Styron INSPIREâ„¢ DLGF 9631.01 Z Polypropylene homopolymer, 60% LGF
- Shin-Etsu Silicones KSP-102 Fluid
- DSM Stanyl® TW200F8 Nylon 46-40% Glass Reinforced (European Grade) (Dry)
- DSM Stanyl® TW275F6 Nylon 46-30% Glass Reinforced, Heat Stabilized, Wear and Friction Modified (Asian Grade) (Cond)
- Epoxy Technology EPO-TEK® H20S Electrically Conductive, Silver Epoxy for Die Stamping
- 3M R3187 Repulpable Single-Coated Tapes
- Arlon 47581R007 0.007" (0.178 mm) Uncured Silicone Rubber with Fiberglass Substrate
- Buckeye Polymers BP RPP 4012 TU Polypropylene, 40% Mineral Filled
Copyright © lookpolymers.com All Rights Reserved