DuPont Performance Polymers Rynite® 415HP BK503 Polyethylene Terephthalate (PET) (Unverified Data**)

Category	Polymer , Thermoplastic , Polyester, TP , Polyethylene Terephthalate (PET) , Polyethylene Terephthalate (PET), 20% Glass Reinforced
Manufacturer	DuPont Performance Polymers
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	DuPont Performance Polymers Rynite® 415HP BK503 Polyethylene Terephthalate (PET) (Unverified Data**).pdf
Price	EMAIL US sales@lookpolymers.com

Material Notes:

15% Glass Reinforced Polyethylene Terephthalate with Excellent Impact Resistance Rynite 415HP BK503 is a 15% glass reinforced modified polyethylene terephthalate with improved for easy fast processing over a broad molding range with excellent balance oInformation provided by DuPont Performance Polymers

Physical Properties	Metric	English	Comments
Density	1.39 g/cc	0.0502 lb/in³	ISO 1183

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	80.0 MPa	11600 psi	ISO 527-1/-2
Elongation at Break	5.0 %	5.0 %	ISO 527-1/-2
Tensile Modulus	4.50 GPa	653 ksi	ISO 527-1/-2
Flexural Modulus	4.00 GPa	580 ksi	ISO 178
Izod Impact, Notched (ISO)	11.0 kJ/m²	5.23 ft-lb/in²	ISO 180/1A
Charpy Impact Unnotched	5.50 J/cm²	26.2 ft-lb/in²	ISO 179/1eU
Charpy Impact, Notched	1.10 J/cm²	5.23 ft-lb/in²	ISO 179/1eA

Thermal Properties	Metric	English	Comments
Melting Point	250 °C	482 °F	10°C/min; ISO 11357-1/-3
Deflection Temperature at 1.8 MPa (264 psi)	190 °C	374 °F	ISO 75-1/-2
Flammability, UL94	HB @Thickness 1.50 mm	HB @Thickness 0.0591 in	IEC 60695-11-10
	HB @Thickness 0.800 mm	HB @Thickness 0.0315 in	IEC 60695-11-10

Electrical Properties	Metric	English	Comments
Comparative Tracking Index	350 V	350 V	IEC 60112

Descriptive Properties	Value	Comments
Part Marking Code	>PET-IGF15<	ISO 11469
Processing	Injection Moulding
Regional Availability	Asia Pacific
	Europe
	Global
	Near East/Africa
	North America
	South and Central America
Resin Identification	PET-IGF15
UL recognition	UL