E-Polymers TEKAMID® TB110M40 , 40% Mineral Filled PA6, DAM
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 40% Mineral Filled |
| Manufacturer | E-Polymers Co. Ltd. |
| Trade Name | TEKAMID® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | E-Polymers TEKAMID® TB110M40 , 40% Mineral Filled PA6, DAM.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
40% Mineral filled, Heat resistance, PlatableInformation provided by E-Polymers Co. Ltd.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.46 g/cc | 0.0527 lb/in³ | ASTM D792 |
| Water Absorption | 1.0 % | 1.0 % | 23°C/24 hr; ASTM D570 |
| Linear Mold Shrinkage | 0.0080 cm/cm | 0.0080 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 116 | 116 | ASTM D786 |
| Tensile Strength, Yield | 85.0 MPa | 12300 psi | ASTM D638 |
| Elongation at Break | 10 % | 10 % | ASTM D638 |
| Flexural Yield Strength | 140 MPa | 20300 psi | ASTM D790 |
| Flexural Modulus | 5.40 GPa | 783 ksi | ASTM D790 |
| Izod Impact, Notched | 0.700 J/cm | 1.31 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 40.0 µm/m-°C @Temperature 20.0 °C |
22.2 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
| Melting Point | 220 °C | 428 °F | ASTM D2133 |
| Deflection Temperature at 0.46 MPa (66 psi) | 200 °C | 392 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 130 °C | 266 °F | ASTM D648 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Arc Resistance | 190 sec | 190 sec | Tungsten electrode; ASTM D495 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 270 - 290 °C | 518 - 554 °F | |
| Mold Temperature | 80.0 - 90.0 °C | 176 - 194 °F |
Users viewing this material also viewed the following:
- Mytex Polymers AN18KW-01 FK Polypropylene, Rubber modified
- Nitriflex SB-1013G Styrene Butadiene Copolymer
- SABIC Innovative Plastics LNP LUBRICOMP OCL36A PPS - Branched
- Teknor Apex ELEXAR® EL 8623 Thermoplastic Elastomer
- Wellman Wellamid® GFT1675-N1 33% Glass Fiber Reinforced, Impact Modified Nylon 66
- Williams Advanced Alloys C118 Solder
- Chevron Phillips Marlex® 9346 HDPE Natural Pipe Resin
- Ensinger Tecapeek® XP-91BHT Compression Molded PEEK HT Compound, 30% Fiberglass, Black Pigmented
- Amity Thermosets ATO 142 Phenolic Molding Organic Filler, Compression Molded
Copyright © lookpolymers.com All Rights Reserved