E-Polymers TEKAMID® TA250GFR , Flame Retardant, 25% Glass Fiber Reinforced PA66, DAM
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Glass Fiber Filled, Flame Retardant |
| Manufacturer | E-Polymers Co. Ltd. |
| Trade Name | TEKAMID® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | E-Polymers TEKAMID® TA250GFR , Flame Retardant, 25% Glass Fiber Reinforced PA66, DAM.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
GF reinforced, Flame RetardantInformation provided by E-Polymers Co. Ltd.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.56 g/cc | 0.0564 lb/in³ | ASTM D792 |
| Water Absorption | 0.60 % | 0.60 % | 23°C/24 hr; ASTM D570 |
| Linear Mold Shrinkage | 0.0050 cm/cm | 0.0050 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 120 | 120 | ASTM D786 |
| Tensile Strength, Yield | 157 MPa | 22800 psi | ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | ASTM D638 |
| Flexural Yield Strength | 220 MPa | 31900 psi | ASTM D790 |
| Flexural Modulus | 8.50 GPa | 1230 ksi | ASTM D790 |
| Izod Impact, Notched | 1.00 J/cm | 1.87 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 60.0 µm/m-°C @Temperature 20.0 °C |
33.3 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
| Melting Point | 260 °C | 500 °F | ASTM D2133 |
| Deflection Temperature at 0.46 MPa (66 psi) | 260 °C | 500 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 250 °C | 482 °F | ASTM D648 |
| Flammability, UL94 | V-0 | V-0 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 270 - 290 °C | 518 - 554 °F | |
| Mold Temperature | 80.0 - 120 °C | 176 - 248 °F |
Users viewing this material also viewed the following:
- Polimeri Europa EDISTIR RK0414 High Impact Polystyrene (HIPS) (discontinued **)
- ExxonMobil Escorene® LD-400 LDPE Medium/High Voltage Insulation (discontinued **)
- SABIC Innovative Plastics Lexan® HP2NR PC (Asia Pacific)
- Hong Kun Group TBTU Pharmaceutical Intermediate
- Imerys Minsparâ„¢ 1 Feldspar
- Greene Tweed FLUORAZ® 790 Fluoroelastomer, FEPM
- Isoflon PSU Polysulfone
- SABIC Innovative Plastics Valox® 830 PBT (Asia Pacific)
- Saint-Gobain Chemlam® SGC6-04 Copper Adhesive Tape
Copyright © lookpolymers.com All Rights Reserved