DuPont™ Tedlar® SP TTR5JAM9 Transparent Polyvinyl Fluoride Film

Category	Polymer , Film , Thermoplastic , Fluoropolymer
Manufacturer	DuPont
Trade Name	Tedlar® SP
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	DuPont™ Tedlar® SP TTR5JAM9 Transparent Polyvinyl Fluoride Film.pdf
Price	EMAIL US sales@lookpolymers.com

Material Notes:

Transparent, Medium Gloss. Tedlar® SP polyvinyl fluoride film is designed to provide excellent conformability to substrates while maintaining the good durability, color stability, chemical resistance, and ease of cleaning expected of PVF film. Tedlar® SP also offers custom color capability not previously available in PVF film. Tedlar® SP is an unoriented film. It possesses high elongation and moderate yield stress. After lamination using conventional means, it can be easily embossed and will maintain high pattern definition. Tedlar® SP can also be subjected to high levels of forming without significant recovery stresses.Information provided by DuPont.

Physical Properties	Metric	English	Comments
Thickness	12.7 microns	0.500 mil

Mechanical Properties	Metric	English	Comments
Tensile Strength	34.0 MPa	4930 psi	ASTM D882-80, Method A - 100%
Elongation at Break	175 %	175 %	ASTM D882-80
Tear Strength	550 kN/m	3140 pli	Graves, MD; ASTM D1004
	550 kN/m	3140 pli	Graves, TD; ASTM D1004

Thermal Properties	Metric	English	Comments
Maximum Service Temperature, Air	107 °C	225 °F	Continuous
	175 °C	347 °F	Short Cycle
Minimum Service Temperature, Air	-72.0 °C	-97.6 °F	Continuous
Shrinkage	<= 2.0 % @Temperature 170 °C	<= 2.0 % @Temperature 338 °F	ASTM D1204-78
	0.60 % @Temperature 50.0 °C, Time 1800 sec	0.60 % @Temperature 122 °F, Time 0.500 hour
	1.1 % @Temperature 100 °C, Time 1800 sec	1.1 % @Temperature 212 °F, Time 0.500 hour
	1.25 % @Temperature 150 °C, Time 1800 sec	1.25 % @Temperature 302 °F, Time 0.500 hour

Optical Properties	Metric	English	Comments
Haze	2.0 %	2.0 %	Internal; Gardner
	33 %	33 %	Total; Gardner
Gloss	6.0 %	6.0 %	20°; Gardner
	27 %	27 %	60°; Gardner
	31 %	31 %	85°; Gardner
Transmission, Visible	90 %	90 %	transparent; thickness not quantified

Electrical Properties	Metric	English	Comments
Volume Resistivity	4.00e+13 ohm-cm	4.00e+13 ohm-cm	ASTM D257-78
Dielectric Constant	7.0	7.0	ASTM D151-81
Dielectric Strength	118 kV/mm	3000 kV/in	ASTM D151-81
Dissipation Factor	0.0020	0.0020	ASTM D151-81

Processing Properties	Metric	English	Comments
Processing Temperature	105 - 171 °C	221 - 340 °F	Film Forming Surface Temperature

Descriptive Properties	Value	Comments
Resistance to Acids	No Visible Effect	2 hr Boiling
Resistance to Bases	No Visible Effect	Immersion