Hexcel® HexWeb® HRH-10 - 1/8- 9.0 Aramid Fiber/Phenolic Resin Honeycomb

Category Other Engineering Material , Composite Core Material , Polymer , Thermoset , Aramid , Phenolic
Manufacturer Hexcel
Trade Name HexWeb®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Hexcel® HexWeb® HRH-10 - 1/8- 9.0 Aramid Fiber/Phenolic Resin Honeycomb.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Designation: Material-Cell Size-Density.Hexweb HRH-10 is manufactured from NOMEX aramid fiber sheets. A thermosetting adhesive is used to bond these sheets at the nodes, and after expanding to the hexagonal or OX-Core confiation, the block is dipped in phenolic resin. After curing the resin, slices are cut to the desired thickness. For special applications, such as air directionalizing, HexWeb HRH-10 can be provided without the phenolic resin. Using this process, a wide range of cell sizes, paper thicknesses, and densities can be produced.Information provided by HexCel
Physical Properties Metric English Comments
Density 0.144 g/cc
0.00521 lb/in³
Mechanical Properties Metric English Comments
Compressive Yield Strength >= 10.51 MPa
>= 1525 psi
Bare, min
>= 11.0 MPa
>= 1600 psi
Stabilized, min
13.8 MPa
2000 psi
Bare, typ
14.5 MPa
2100 psi
Stabilized, typ
Compressive Modulus 0.621 GPa
90.0 ksi
Stabilized, typ
Shear Modulus 0.0758 GPa
11.0 ksi
Plate Shear, W Direction, typ
0.121 GPa
17.5 ksi
Plate Shear, L Direction, typ
Shear Strength >= 1.72 MPa
>= 250 psi
Plate Shear, W Direction, min
2.07 MPa
300 psi
Plate Shear, W Direction, typ
>= 2.93 MPa
>= 425 psi
Plate Shear, L Direction, min
3.55 MPa
515 psi
Plate Shear, L Direction, typ