DuPont Performance Polymers Hytrel® G3548L TPC-ET (Unverified Data**)
| Category | Polymer , Thermoplastic , Elastomer, TPE , Polyester, TP , Polyester Thermoplastic Elastomer |
| Manufacturer | DuPont Performance Polymers |
| Trade Name | Hytrel® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | DuPont Performance Polymers Hytrel® G3548L TPC-ET
(Unverified Data**).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Hytrel® G3548L is a low modulus grade with nominal hardness of 35D. It contains non-discoloring stabilizer. It can be processed by many conventional thermoplastic processing techniques like injection molding and extrusion.Information provided by DuPont Performance Polymers
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.15 g/cc | 1.15 g/cc | ASTM D792 |
| Density | 1.15 g/cc | 0.0415 lb/in³ | ISO 1183 |
| Water Absorption | 5.0 % @Temperature 23.0 °C |
5.0 % @Temperature 73.4 °F |
Immersion 24h; ASTM D570 |
| 5.0 % @Temperature 23.0 °C |
5.0 % @Temperature 73.4 °F |
Immersion 24h; ISO 62 | |
| Linear Mold Shrinkage | 0.0050 cm/cm | 0.0050 in/in | Flow; ASTM D955 |
| Linear Mold Shrinkage, Flow | 0.010 cm/cm @Thickness 2.00 mm |
0.010 in/in @Thickness 0.0787 in |
ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.010 cm/cm @Thickness 2.00 mm |
0.010 in/in @Thickness 0.0787 in |
ISO 294-4 |
| Melt Flow | 10 g/10 min @Load 2.16 kg, Temperature 190 °C |
10 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| 10 g/10 min @Load 2.16 kg, Temperature 190 °C |
10 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | <= 35 | <= 35 | ASTM D2240 |
| <= 35 | <= 35 | ISO 868 | |
| 26 @Time 15.0 sec |
26 @Time 0.00417 hour |
ISO 868 | |
| Tensile Strength at Break | 9.70 MPa @Temperature 23.0 °C |
1410 psi @Temperature 73.4 °F |
ISO 527 (1BA bar) |
| 10.3 MPa @Temperature 23.0 °C |
1490 psi @Temperature 73.4 °F |
ASTM D638 | |
| Tensile Stress | 1.70 MPa @Strain 5.00 %, Temperature 23.0 °C |
247 psi @Strain 5.00 %, Temperature 73.4 °F |
ASTM D638 |
| 2.50 MPa @Strain 10.0 %, Temperature 23.0 °C |
363 psi @Strain 10.0 %, Temperature 73.4 °F |
ISO 527 (1BA bar) | |
| 2.60 MPa @Strain 10.0 %, Temperature 23.0 °C |
377 psi @Strain 10.0 %, Temperature 73.4 °F |
ASTM D638 | |
| Elongation at Break | 200 % @Temperature 23.0 °C |
200 % @Temperature 73.4 °F |
ASTM D638 |
| 240 % @Temperature 23.0 °C |
240 % @Temperature 73.4 °F |
ISO 527 (1BA bar) | |
| Tensile Modulus | 0.0230 GPa @Temperature 23.0 °C |
3.34 ksi @Temperature 73.4 °F |
ISO 527 |
| Flexural Modulus | 0.00700 GPa @Temperature 100 °C |
1.02 ksi @Temperature 212 °F |
ASTM D790 |
| 0.00700 GPa @Temperature 100 °C |
1.02 ksi @Temperature 212 °F |
ISO 178 | |
| 0.0320 GPa @Temperature 23.0 °C |
4.64 ksi @Temperature 73.4 °F |
ISO 178 | |
| 0.0324 GPa @Temperature 23.0 °C |
4.70 ksi @Temperature 73.4 °F |
ASTM D790 | |
| 0.0500 GPa @Temperature -40.0 °C |
7.25 ksi @Temperature -40.0 °F |
ISO 178 | |
| 0.0620 GPa @Temperature -40.0 °C |
8.99 ksi @Temperature -40.0 °F |
ASTM D790 | |
| Izod Impact, Notched | NB @Temperature -40.0 °C |
NB @Temperature -40.0 °F |
ASTM D256 |
| NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
ASTM D256 | |
| Izod Impact, Notched (ISO) | NB @Temperature -40.0 °C |
NB @Temperature -40.0 °F |
ISO 180/1A |
| Charpy Impact, Notched | NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 500 µm/m-°C @Temperature -40.0 - 23.0 °C |
278 µin/in-°F @Temperature -40.0 - 73.4 °F |
ASTM E 831 |
| 500 µm/m-°C @Temperature 23.0 - 55.0 °C |
278 µin/in-°F @Temperature 73.4 - 131 °F |
ASTM E 831 | |
| 500 µm/m-°C @Temperature -40.0 - 23.0 °C |
278 µin/in-°F @Temperature -40.0 - 73.4 °F |
ISO 11359-1/-2 | |
| 500 µm/m-°C @Temperature 23.0 - 55.0 °C |
278 µin/in-°F @Temperature 73.4 - 131 °F |
ISO 11359-1/-2 | |
| CTE, linear, Transverse to Flow | 220 µm/m-°C @Temperature -40.0 - 23.0 °C |
122 µin/in-°F @Temperature -40.0 - 73.4 °F |
ASTM E 831 |
| 220 µm/m-°C @Temperature -40.0 - 23.0 °C |
122 µin/in-°F @Temperature -40.0 - 73.4 °F |
ISO 11359-1/-2 | |
| 240 µm/m-°C @Temperature 23.0 - 55.0 °C |
133 µin/in-°F @Temperature 73.4 - 131 °F |
ASTM E 831 | |
| 240 µm/m-°C @Temperature 23.0 - 55.0 °C |
133 µin/in-°F @Temperature 73.4 - 131 °F |
ISO 11359-1/-2 | |
| 310 µm/m-°C @Temperature 55.0 - 120 °C |
172 µin/in-°F @Temperature 131 - 248 °F |
ASTM E 831 | |
| 310 µm/m-°C @Temperature 55.0 - 120 °C |
172 µin/in-°F @Temperature 131 - 248 °F |
ISO 11359-1/-2 | |
| Melting Point | 154 °C | 309 °F | 10°C/min; ISO 11357-1/-3 |
| 156 °C | 313 °F | ASTM D3418 | |
| Brittleness Temperature | -61.0 °C | -77.8 °F | ISO 974 |
| UL RTI, Electrical | 50.0 °C @Thickness 1.50 mm |
122 °F @Thickness 0.0591 in |
UL 746B |
| 50.0 °C @Thickness 3.00 mm |
122 °F @Thickness 0.118 in |
UL 746B | |
| UL RTI, Mechanical with Impact | 50.0 °C @Thickness 3.00 mm |
122 °F @Thickness 0.118 in |
UL 746B |
| 50.0 °C @Thickness 1.50 mm |
122 °F @Thickness 0.0591 in |
UL 746B | |
| UL RTI, Mechanical without Impact | 50.0 °C @Thickness 1.50 mm |
122 °F @Thickness 0.0591 in |
UL 746B |
| 50.0 °C @Thickness 3.00 mm |
122 °F @Thickness 0.118 in |
UL 746B | |
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
IEC 60695-11-10 |
| HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
IEC 60695-11-10 | |
| HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
UL94 | |
| HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
UL94 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Comparative Tracking Index | >= 600 V @Thickness 3.00 mm, Temperature 23.0 °C |
>= 600 V @Thickness 0.118 in, Temperature 73.4 °F |
UL 746A |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 180 °C | 356 °F | Optimum; Extrusion |
| 190 °C | 374 °F | Optimum; Injection Molding | |
| Mold Temperature | 30.0 - 40.0 °C | 86.0 - 104 °F | Injection Molding |
| 40.0 °C | 104 °F | optimum; Injection Molding | |
| Drying Temperature | 80.0 °C | 176 °F | Extrusion |
| 80.0 °C | 176 °F | Injection Molding | |
| Dry Time | 2.00 - 3.00 hour | 2.00 - 3.00 hour | Extrusion |
| 2.00 - 3.00 hour | 2.00 - 3.00 hour | Injection Molding | |
| Moisture Content | <= 0.080 % | <= 0.080 % | Extrusion |
| <= 0.080 % | <= 0.080 % | Injection Molding |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Additive | Antioxidant | |
| Appearance | Beige, Light | |
| Drying Recommended | Yes | |
| Extrudable - Blown Film | Yes | |
| Extrudable - Cast Film | Yes | |
| Extrudable - Coating | Yes | |
| Extrudable - Filament | Yes | |
| Extrudable - Hose | Yes | |
| Extrudable - Sheet | Yes | |
| Extrudable - Tubing | Yes | |
| Extrudable - Wire and Cable | Yes | |
| Extrusion Blow Moldable | Yes | |
| Features | Color Stability, Good | |
| Copolymer, Block | ||
| General Purpose | ||
| Hardness, Low | ||
| Forms | Pellets | |
| Generic | TPC-ET | |
| Heat Stabilized | Yes | |
| Injection Blow Moldable | Yes | |
| Material Status | Current | |
| Melt Castable | Yes | |
| Part Marking Code | >TPC-ET< | ISO 11469 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® DMX9455 PC Copolymer (Asia Pacific)
- Plansee DENAL® 920 60 20 Tungsten-Nickel-Iron-Cobalt Alloy
- Fujipoly Industries Sarcon® NR-c Gap Filler Pad Non-Silicone
- Haynes 214® alloy, 50% cold reduction, 1095°C (2000°F) for 5 minutes
- Samsung Cheil Industries Starex® SG-501 Expandable Polystyrene (EPS) High Expansion
- A. Schulman SCHULAMID® 66 MK40HI 40% Mineral Reinforced, Impact Modified 66
- Trelleborg S565 Silicone Rubber
Copyright © lookpolymers.com All Rights Reserved