DuPont Performance Polymers Delrin® 570 NC000 Acetal (POM)  (Unverified Data**)

Category Polymer , Thermoplastic , Acetal (POM) , Acetal Homopolymer, Glass Fiber Reinforced
Manufacturer DuPont Performance Polymers
Trade Name Delrin®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Delrin® 570 NC000 Acetal (POM)  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
20% Glass Filled Medium Viscosity Acetal Homopolymer Delrin 570 NC000 is a medium viscosity acetal homopolymer containing 20% glass fiber filler for injection molding. Delrin 570 has very high stiffness low warpage and good creep resistance.Information provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.56 g/cc
0.0564 lb/in³
ISO 1183
Water Absorption 0.80 %

@Thickness 2.00 mm
0.80 %

@Thickness 0.0787 in
Sim. to ISO 62
Moisture Absorption 0.100 %

@Thickness 2.00 mm
0.100 %

@Thickness 0.0787 in
Sim. to ISO 62
Viscosity 96000 cP

@Shear Rate 5000 1/s,
Temperature 230 °C
96000 cP

@Shear Rate 5000 1/s,
Temperature 446 °F
ISO 11403-1 -2
102000 cP

@Shear Rate 5000 1/s,
Temperature 215 °C
102000 cP

@Shear Rate 5000 1/s,
Temperature 419 °F
ISO 11403-1 -2
108000 cP

@Shear Rate 5000 1/s,
Temperature 200 °C
108000 cP

@Shear Rate 5000 1/s,
Temperature 392 °F
ISO 11403-1 -2
345000 cP

@Shear Rate 500 1/s,
Temperature 230 °C
345000 cP

@Shear Rate 500 1/s,
Temperature 446 °F
ISO 11403-1 -2
384000 cP

@Shear Rate 500 1/s,
Temperature 215 °C
384000 cP

@Shear Rate 500 1/s,
Temperature 419 °F
ISO 11403-1 -2
428000 cP

@Shear Rate 500 1/s,
Temperature 200 °C
428000 cP

@Shear Rate 500 1/s,
Temperature 392 °F
ISO 11403-1 -2
Linear Mold Shrinkage, Flow 0.018 cm/cm
0.018 in/in
ISO 294-4 2577
Linear Mold Shrinkage, Transverse 0.012 cm/cm
0.012 in/in
ISO 294-4 2577
Melt Flow 7.0 g/10 min

@Load 2.16 kg,
Temperature 190 °C
7.0 g/10 min

@Load 4.76 lb,
Temperature 374 °F
cm³/10min; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 53.0 MPa
7690 psi
ISO 527-1/-2
Elongation at Break 12 %
12 %
ISO 527-1/-2
Tensile Modulus 4.90 GPa
711 ksi
ISO 527-1/-2
Flexural Modulus 4.60 GPa
667 ksi
ISO 178
Izod Impact, Notched (ISO) 6.00 kJ/m²
2.86 ft-lb/in²
ISO 180/1A
Charpy Impact Unnotched 5.40 J/cm²
25.7 ft-lb/in²
ISO 179/1eU
5.00 J/cm²

@Temperature -30.0 °C
23.8 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eU
Charpy Impact, Notched 0.350 J/cm²
1.67 ft-lb/in²
ISO 179/1eA
0.300 J/cm²

@Temperature -30.0 °C
1.43 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 60.0 µm/m-°C
33.3 µin/in-°F
ISO 11359-1/-2
CTE, linear, Transverse to Flow 85.0 µm/m-°C
47.2 µin/in-°F
ISO 11359-1/-2
Melting Point 178 °C
352 °F
10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi) 165 °C
329 °F
ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 125 °C
257 °F
ISO 75-1/-2
Vicat Softening Point 160 °C
320 °F
50°C/h 50N; ISO 306
Flammability, UL94 HB

@Thickness 1.50 mm
HB

@Thickness 0.0591 in
IEC 60695-11-10
Flame Spread 53 mm/min

@Thickness 1.00 mm
2.1 in/min

@Thickness 0.0394 in
ISO 3795 (FMVSS 302)
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+15 ohm-cm
1.00e+15 ohm-cm
IEC 60093
Surface Resistance >= 1.00e+15 ohm
>= 1.00e+15 ohm
IEC 60093
Dielectric Constant 3.9

@Frequency 100 Hz
3.9

@Frequency 100 Hz
IEC 60250
3.9

@Frequency 1.00e+6 Hz
3.9

@Frequency 1.00e+6 Hz
IEC 60250
Comparative Tracking Index 600 V
600 V
IEC 60112
Descriptive Properties Value Comments
Additives Release agent
Delivery Form Pellets
Part Marking Code >POM-GF20<
ISO 11469
Processing Injection Moulding
Regional Availability Asia Pacific
Europe
Global
Near East/Africa
North America
South and Central America
Resin Identification POM-GF20