DuPont Performance Polymers Delrin® 511P BK402 Acetal Homopolymer

Category Polymer , Thermoplastic , Acetal (POM)
Manufacturer DuPont Performance Polymers
Trade Name Delrin®
Port Shanghai port,China
Trade Terms EXW, FOB, CFR, CIF
Payment Terms L/C, T/T, PayPal
Download PDF DuPont Performance Polymers Delrin® 511P BK402 Acetal Homopolymer.pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
Delrin® 511P is a medium viscosity acetal homopolymer with improved thermal stability and modifications for more precise molding(reduced warpage, less shrinkage, fewer voids).Information provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.42 g/cc
0.0513 lb/in³
ISO 1183
Water Absorption 0.20 %
<br>@Temperature 23.0 °C
 0.20 %
<br>@Temperature 73.4 °F
 Equilibrium 50%RH; ISO 62, Similar to
1.0 %
<br>@Temperature 23.0 °C
 1.0 %
<br>@Temperature 73.4 °F
 Saturation, immersed; ISO 62, Similar to
Linear Mold Shrinkage, Flow 0.017 cm/cm
<br>@Thickness 2.00 mm
 0.017 in/in
<br>@Thickness 0.0787 in
 ISO 294-4
Linear Mold Shrinkage, Transverse 0.017 cm/cm
<br>@Thickness 2.00 mm
 0.017 in/in
<br>@Thickness 0.0787 in
 ISO 294-4
Melt Flow 14 g/10 min
<br>@Load 2.16 kg,<br> Temperature 190 °C
 14 g/10 min
<br>@Load 4.76 lb,<br> Temperature 374 °F
 ISO 1133
Mechanical Properties Metric English Comments
Tensile Stress 0.830 MPa
<br>@Strain 0.100 %,<br> Temperature 100 °C
 120 psi
<br>@Strain 0.100 %,<br> Temperature 212 °F
 ISO 11403-1/-2
1.13 MPa
<br>@Strain 0.100 %,<br> Temperature 80.0 °C
 164 psi
<br>@Strain 0.100 %,<br> Temperature 176 °F
 ISO 11403-1/-2
2.24 MPa
<br>@Strain 0.100 %,<br> Temperature 23.0 °C
 325 psi
<br>@Strain 0.100 %,<br> Temperature 73.4 °F
 ISO 11403-1/-2
2.56 MPa
<br>@Strain 0.200 %,<br> Temperature 100 °C
 371 psi
<br>@Strain 0.200 %,<br> Temperature 212 °F
 ISO 11403-1/-2
2.80 MPa
<br>@Strain 0.100 %,<br> Temperature -40.0 °C
 406 psi
<br>@Strain 0.100 %,<br> Temperature -40.0 °F
 ISO 11403-1/-2
3.40 MPa
<br>@Strain 0.200 %,<br> Temperature 80.0 °C
 493 psi
<br>@Strain 0.200 %,<br> Temperature 176 °F
 ISO 11403-1/-2
3.83 MPa
<br>@Strain 0.300 %,<br> Temperature 100 °C
 555 psi
<br>@Strain 0.300 %,<br> Temperature 212 °F
 ISO 11403-1/-2
4.58 MPa
<br>@Strain 0.400 %,<br> Temperature 100 °C
 664 psi
<br>@Strain 0.400 %,<br> Temperature 212 °F
 ISO 11403-1/-2
5.08 MPa
<br>@Strain 0.300 %,<br> Temperature 80.0 °C
 737 psi
<br>@Strain 0.300 %,<br> Temperature 176 °F
 ISO 11403-1/-2
6.17 MPa
<br>@Strain 0.500 %,<br> Temperature 100 °C
 895 psi
<br>@Strain 0.500 %,<br> Temperature 212 °F
 ISO 11403-1/-2
6.41 MPa
<br>@Strain 0.400 %,<br> Temperature 80.0 °C
 930 psi
<br>@Strain 0.400 %,<br> Temperature 176 °F
 ISO 11403-1/-2
6.77 MPa
<br>@Strain 0.200 %,<br> Temperature 23.0 °C
 982 psi
<br>@Strain 0.200 %,<br> Temperature 73.4 °F
 ISO 11403-1/-2
7.51 MPa
<br>@Strain 0.600 %,<br> Temperature 100 °C
 1090 psi
<br>@Strain 0.600 %,<br> Temperature 212 °F
 ISO 11403-1/-2
8.21 MPa
<br>@Strain 0.700 %,<br> Temperature 100 °C
 1190 psi
<br>@Strain 0.700 %,<br> Temperature 212 °F
 ISO 11403-1/-2
8.52 MPa
<br>@Strain 0.200 %,<br> Temperature -40.0 °C
 1240 psi
<br>@Strain 0.200 %,<br> Temperature -40.0 °F
 ISO 11403-1/-2
8.53 MPa
<br>@Strain 0.500 %,<br> Temperature 80.0 °C
 1240 psi
<br>@Strain 0.500 %,<br> Temperature 176 °F
 ISO 11403-1/-2
9.28 MPa
<br>@Strain 0.800 %,<br> Temperature 100 °C
 1350 psi
<br>@Strain 0.800 %,<br> Temperature 212 °F
 ISO 11403-1/-2
9.95 MPa
<br>@Strain 0.600 %,<br> Temperature 80.0 °C
 1440 psi
<br>@Strain 0.600 %,<br> Temperature 176 °F
 ISO 11403-1/-2
10.25 MPa
<br>@Strain 0.300 %,<br> Temperature 23.0 °C
 1487 psi
<br>@Strain 0.300 %,<br> Temperature 73.4 °F
 ISO 11403-1/-2
10.25 MPa
<br>@Strain 0.900 %,<br> Temperature 100 °C
 1487 psi
<br>@Strain 0.900 %,<br> Temperature 212 °F
 ISO 11403-1/-2
10.95 MPa
<br>@Strain 1.00 %,<br> Temperature 100 °C
 1588 psi
<br>@Strain 1.00 %,<br> Temperature 212 °F
 ISO 11403-1/-2
11.4 MPa
<br>@Strain 0.700 %,<br> Temperature 80.0 °C
 1650 psi
<br>@Strain 0.700 %,<br> Temperature 176 °F
 ISO 11403-1/-2
12.07 MPa
<br>@Strain 1.10 %,<br> Temperature 100 °C
 1751 psi
<br>@Strain 1.10 %,<br> Temperature 212 °F
 ISO 11403-1/-2
12.36 MPa
<br>@Strain 0.800 %,<br> Temperature 80.0 °C
 1793 psi
<br>@Strain 0.800 %,<br> Temperature 176 °F
 ISO 11403-1/-2
12.89 MPa
<br>@Strain 0.400 %,<br> Temperature 23.0 °C
 1870 psi
<br>@Strain 0.400 %,<br> Temperature 73.4 °F
 ISO 11403-1/-2
12.92 MPa
<br>@Strain 0.300 %,<br> Temperature -40.0 °C
 1874 psi
<br>@Strain 0.300 %,<br> Temperature -40.0 °F
 ISO 11403-1/-2
13.19 MPa
<br>@Strain 1.20 %,<br> Temperature 100 °C
 1913 psi
<br>@Strain 1.20 %,<br> Temperature 212 °F
 ISO 11403-1/-2
13.59 MPa
<br>@Strain 0.900 %,<br> Temperature 80.0 °C
 1971 psi
<br>@Strain 0.900 %,<br> Temperature 176 °F
 ISO 11403-1/-2
13.98 MPa
<br>@Strain 1.30 %,<br> Temperature 100 °C
 2028 psi
<br>@Strain 1.30 %,<br> Temperature 212 °F
 ISO 11403-1/-2
14.76 MPa
<br>@Strain 1.40 %,<br> Temperature 100 °C
 2141 psi
<br>@Strain 1.40 %,<br> Temperature 212 °F
 ISO 11403-1/-2
15.17 MPa
<br>@Strain 1.00 %,<br> Temperature 80.0 °C
 2200 psi
<br>@Strain 1.00 %,<br> Temperature 176 °F
 ISO 11403-1/-2
15.61 MPa
<br>@Strain 1.50 %,<br> Temperature 100 °C
 2264 psi
<br>@Strain 1.50 %,<br> Temperature 212 °F
 ISO 11403-1/-2
16.2 MPa
<br>@Strain 0.400 %,<br> Temperature -40.0 °C
 2350 psi
<br>@Strain 0.400 %,<br> Temperature -40.0 °F
 ISO 11403-1/-2
16.27 MPa
<br>@Strain 1.10 %,<br> Temperature 80.0 °C
 2360 psi
<br>@Strain 1.10 %,<br> Temperature 176 °F
 ISO 11403-1/-2
16.33 MPa
<br>@Strain 1.60 %,<br> Temperature 100 °C
 2368 psi
<br>@Strain 1.60 %,<br> Temperature 212 °F
 ISO 11403-1/-2
17.03 MPa
<br>@Strain 1.70 %,<br> Temperature 100 °C
 2470 psi
<br>@Strain 1.70 %,<br> Temperature 212 °F
 ISO 11403-1/-2
17.34 MPa
<br>@Strain 0.500 %,<br> Temperature 23.0 °C
 2515 psi
<br>@Strain 0.500 %,<br> Temperature 73.4 °F
 ISO 11403-1/-2
17.43 MPa
<br>@Strain 1.20 %,<br> Temperature 80.0 °C
 2528 psi
<br>@Strain 1.20 %,<br> Temperature 176 °F
 ISO 11403-1/-2
17.73 MPa
<br>@Strain 1.80 %,<br> Temperature 100 °C
 2572 psi
<br>@Strain 1.80 %,<br> Temperature 212 °F
 ISO 11403-1/-2
18.37 MPa
<br>@Strain 1.90 %,<br> Temperature 100 °C
 2664 psi
<br>@Strain 1.90 %,<br> Temperature 212 °F
 ISO 11403-1/-2
18.53 MPa
<br>@Strain 1.30 %,<br> Temperature 80.0 °C
 2688 psi
<br>@Strain 1.30 %,<br> Temperature 176 °F
 ISO 11403-1/-2
19.04 MPa
<br>@Strain 2.00 %,<br> Temperature 100 °C
 2762 psi
<br>@Strain 2.00 %,<br> Temperature 212 °F
 ISO 11403-1/-2
19.49 MPa
<br>@Strain 1.40 %,<br> Temperature 80.0 °C
 2827 psi
<br>@Strain 1.40 %,<br> Temperature 176 °F
 ISO 11403-1/-2
19.68 MPa
<br>@Strain 2.10 %,<br> Temperature 100 °C
 2854 psi
<br>@Strain 2.10 %,<br> Temperature 212 °F
 ISO 11403-1/-2
20.38 MPa
<br>@Strain 2.20 %,<br> Temperature 100 °C
 2956 psi
<br>@Strain 2.20 %,<br> Temperature 212 °F
 ISO 11403-1/-2
20.53 MPa
<br>@Strain 1.50 %,<br> Temperature 80.0 °C
 2978 psi
<br>@Strain 1.50 %,<br> Temperature 176 °F
 ISO 11403-1/-2
20.85 MPa
<br>@Strain 2.30 %,<br> Temperature 100 °C
 3024 psi
<br>@Strain 2.30 %,<br> Temperature 212 °F
 ISO 11403-1/-2
21.43 MPa
<br>@Strain 2.40 %,<br> Temperature 100 °C
 3108 psi
<br>@Strain 2.40 %,<br> Temperature 212 °F
 ISO 11403-1/-2
21.44 MPa
<br>@Strain 0.500 %,<br> Temperature -40.0 °C
 3110 psi
<br>@Strain 0.500 %,<br> Temperature -40.0 °F
 ISO 11403-1/-2
21.46 MPa
<br>@Strain 1.60 %,<br> Temperature 80.0 °C
 3113 psi
<br>@Strain 1.60 %,<br> Temperature 176 °F
 ISO 11403-1/-2
21.95 MPa
<br>@Strain 2.50 %,<br> Temperature 100 °C
 3184 psi
<br>@Strain 2.50 %,<br> Temperature 212 °F
 ISO 11403-1/-2
22.39 MPa
<br>@Strain 1.70 %,<br> Temperature 80.0 °C
 3247 psi
<br>@Strain 1.70 %,<br> Temperature 176 °F
 ISO 11403-1/-2
22.48 MPa
<br>@Strain 2.60 %,<br> Temperature 100 °C
 3260 psi
<br>@Strain 2.60 %,<br> Temperature 212 °F
 ISO 11403-1/-2
22.54 MPa
<br>@Strain 0.600 %,<br> Temperature 23.0 °C
 3269 psi
<br>@Strain 0.600 %,<br> Temperature 73.4 °F
 ISO 11403-1/-2
23.06 MPa
<br>@Strain 2.70 %,<br> Temperature 100 °C
 3345 psi
<br>@Strain 2.70 %,<br> Temperature 212 °F
 ISO 11403-1/-2
23.26 MPa
<br>@Strain 1.80 %,<br> Temperature 80.0 °C
 3374 psi
<br>@Strain 1.80 %,<br> Temperature 176 °F
 ISO 11403-1/-2
23.47 MPa
<br>@Strain 2.80 %,<br> Temperature 100 °C
 3404 psi
<br>@Strain 2.80 %,<br> Temperature 212 °F
 ISO 11403-1/-2
23.76 MPa
<br>@Strain 2.90 %,<br> Temperature 100 °C
 3446 psi
<br>@Strain 2.90 %,<br> Temperature 212 °F
 ISO 11403-1/-2