Arlon 55359R062 62 mil Uncured/Cured Silicone Rubber with Fiberglass Substrate

Category	Polymer , Thermoset , Silicone , Silicone, Molded, Glass Fiber Filled
Manufacturer	Arlon
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Arlon 55359R062 62 mil Uncured/Cured Silicone Rubber with Fiberglass Substrate.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Design/Construction:Interleave: 3 mil PELayer 2: Uncured Silicone RubberLayer 1: Cured Silicone RubberSubstrate: Style 162 FiberglassThis data represents typical values for the production material and should not be used as material specifications.Information provided by ARLON Silicone Technologies Division.

Physical Properties	Metric	English	Comments
Density	1.30 g/cc	0.0470 lb/in³	Silicone Property; Arlon SQA-TMS-024
Thickness	127 microns	5.00 mil	Layer 1; Arlon SQA-TMS-003
	457 microns	18.0 mil	Substrate
	991 microns	39.0 mil	Layer 2; Arlon SQA-TMS-003
	1570 microns	62.0 mil	Overall Thickness; Arlon SQA-TMS-003

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	50	50	Silicone Property; Arlon SQA-TMS-014
Tensile Strength	4.41 MPa	640 psi	Silicone Property; Arlon SQA-TMS-006
Elongation at Break	170 %	170 %	Silicone Property; Arlon SQA-TMS-006
Peel Strength	1.47 kN/m	8.40 pli	Bond Strength; ASTM D624

Thermal Properties	Metric	English	Comments
Maximum Service Temperature, Inert	232 °C	450 °F
Minimum Service Temperature, Air	-56.7 °C	-70.0 °F

Electrical Properties	Metric	English	Comments
Dielectric Strength	20.1 kV/mm	510 kV/in	ASTM D149

Processing Properties	Metric	English	Comments
Cure Time	120 min @Temperature 204 °C	2.00 hour @Temperature 400 °F	Recommended Post Cure Cycle
	15.0 min @Pressure 0.345 MPa, Temperature 177 °C	0.250 hour @Pressure 50.0 psi, Temperature 350 °F	Recommended Cure Cycle
Shelf Life	6.00 Month @Temperature 23.9 °C	6.00 Month @Temperature 75.0 °F

Descriptive Properties	Value	Comments
Color	Red
Total Product Weight (oz/yd2)	65	Arlon SQA-TMS-025