DuPont Performance Polymers Delrin® 500AF Acetal (POM)  (Unverified Data**)

Category Polymer , Thermoplastic , Acetal (POM) , Acetal Homopolymer, Unreinforced
Manufacturer DuPont Performance Polymers
Trade Name Delrin®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Delrin® 500AF Acetal (POM)  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
20% Teflon® Fiber Filled Medium Viscosity Acetal Homopolymer with Low Wear and Low Friction Delrin 500AF is a medium viscosity acetal homopolymer resin containing 20% Teflon PTFE fibers. It is designed for applications requiring low wear and/or low coeInformation provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.53 g/cc
0.0553 lb/in³
ISO 1183
Water Absorption 1.0 %

@Thickness 2.00 mm
 1.0 %

@Thickness 0.0787 in
 Sim. to ISO 62
Moisture Absorption 0.200 %

@Thickness 2.00 mm
 0.200 %

@Thickness 0.0787 in
 Sim. to ISO 62
Viscosity 100000 cP

@Shear Rate 5000 1/s,
Temperature 230 °C
 100000 cP

@Shear Rate 5000 1/s,
Temperature 446 °F
 ISO 11403-1 -2
107000 cP

@Shear Rate 5000 1/s,
Temperature 215 °C
 107000 cP

@Shear Rate 5000 1/s,
Temperature 419 °F
 ISO 11403-1 -2
116000 cP

@Shear Rate 5000 1/s,
Temperature 200 °C
 116000 cP

@Shear Rate 5000 1/s,
Temperature 392 °F
 ISO 11403-1 -2
374000 cP

@Shear Rate 500 1/s,
Temperature 230 °C
 374000 cP

@Shear Rate 500 1/s,
Temperature 446 °F
 ISO 11403-1 -2
425000 cP

@Shear Rate 500 1/s,
Temperature 215 °C
 425000 cP

@Shear Rate 500 1/s,
Temperature 419 °F
 ISO 11403-1 -2
483000 cP

@Shear Rate 500 1/s,
Temperature 200 °C
 483000 cP

@Shear Rate 500 1/s,
Temperature 392 °F
 ISO 11403-1 -2
Linear Mold Shrinkage, Flow 0.020 cm/cm
0.020 in/in
ISO 294-4 2577
Linear Mold Shrinkage, Transverse 0.014 cm/cm
0.014 in/in
ISO 294-4 2577
Mechanical Properties Metric English Comments
Tensile Strength at Break 50.0 MPa
7250 psi
ISO 527-1/-2
Tensile Stress 8.70 MPa

@Strain 0.900 %,
Temperature 90.0 °C
 1260 psi

@Strain 0.900 %,
Temperature 194 °F
 ISO 11403-1 -2
21.5 MPa

@Strain 3.60 %,
Temperature 90.0 °C
 3120 psi

@Strain 3.60 %,
Temperature 194 °F
 ISO 11403-1 -2
23.9 MPa

@Strain 6.20 %,
Temperature 90.0 °C
 3470 psi

@Strain 6.20 %,
Temperature 194 °F
 ISO 11403-1 -2
24.3 MPa

@Strain 8.90 %,
Temperature 90.0 °C
 3520 psi

@Strain 8.90 %,
Temperature 194 °F
 ISO 11403-1 -2
27.2 MPa

@Strain 1.40 %,
Temperature 40.0 °C
 3950 psi

@Strain 1.40 %,
Temperature 104 °F
 ISO 11403-1 -2
30.5 MPa

@Strain 1.00 %,
Temperature 0.000 °C
 4420 psi

@Strain 1.00 %,
Temperature 32.0 °F
 ISO 11403-1 -2
31.6 MPa

@Strain 1.20 %,
Temperature 23.0 °C
 4580 psi

@Strain 1.20 %,
Temperature 73.4 °F
 ISO 11403-1 -2
32.0 MPa

@Strain 0.900 %,
Temperature -20.0 °C
 4640 psi

@Strain 0.900 %,
Temperature -4.00 °F
 ISO 11403-1 -2
40.5 MPa

@Strain 5.40 %,
Temperature 40.0 °C
 5870 psi

@Strain 5.40 %,
Temperature 104 °F
 ISO 11403-1 -2
42.2 MPa

@Strain 9.40 %,
Temperature 40.0 °C
 6120 psi

@Strain 9.40 %,
Temperature 104 °F
 ISO 11403-1 -2
42.6 MPa

@Strain 13.4 %,
Temperature 40.0 °C
 6180 psi

@Strain 13.4 %,
Temperature 104 °F
 ISO 11403-1 -2
45.6 MPa

@Strain 5.00 %,
Temperature 23.0 °C
 6610 psi

@Strain 5.00 %,
Temperature 73.4 °F
 ISO 11403-1 -2
47.3 MPa

@Strain 8.70 %,
Temperature 23.0 °C
 6860 psi

@Strain 8.70 %,
Temperature 73.4 °F
 ISO 11403-1 -2
47.8 MPa

@Strain 12.4 %,
Temperature 23.0 °C
 6930 psi

@Strain 12.4 %,
Temperature 73.4 °F
 ISO 11403-1 -2
50.2 MPa

@Strain 3.80 %,
Temperature 0.000 °C
 7280 psi

@Strain 3.80 %,
Temperature 32.0 °F
 ISO 11403-1 -2
53.7 MPa

@Strain 6.60 %,
Temperature 0.000 °C
 7790 psi

@Strain 6.60 %,
Temperature 32.0 °F
 ISO 11403-1 -2
54.4 MPa

@Strain 9.50 %,
Temperature 0.000 °C
 7890 psi

@Strain 9.50 %,
Temperature 32.0 °F
 ISO 11403-1 -2
54.9 MPa

@Strain 3.70 %,
Temperature -20.0 °C
 7960 psi

@Strain 3.70 %,
Temperature -4.00 °F
 ISO 11403-1 -2
58.2 MPa

@Strain 6.50 %,
Temperature -20.0 °C
 8440 psi

@Strain 6.50 %,
Temperature -4.00 °F
 ISO 11403-1 -2
59.2 MPa

@Strain 9.30 %,
Temperature -20.0 °C
 8590 psi

@Strain 9.30 %,
Temperature -4.00 °F
 ISO 11403-1 -2
Elongation at Break 10 %
10 %
ISO 527-1/-2
Tensile Modulus 2.80 GPa
406 ksi
ISO 527-1/-2
Flexural Modulus 2.50 GPa
363 ksi
ISO 178
Shear Modulus 0.141 GPa

@Temperature 150 °C
 20.5 ksi

@Temperature 302 °F
 Dynamic; ISO 11403-1 -2
0.306 GPa

@Temperature 110 °C
 44.4 ksi

@Temperature 230 °F
 Dynamic; ISO 11403-1 -2
0.628 GPa

@Temperature 60.0 °C
 91.1 ksi

@Temperature 140 °F
 Dynamic; ISO 11403-1 -2
0.961 GPa

@Temperature 10.0 °C
 139 ksi

@Temperature 50.0 °F
 Dynamic; ISO 11403-1 -2
1.12 GPa

@Temperature -20.0 °C
 162 ksi

@Temperature -4.00 °F
 Dynamic; ISO 11403-1 -2
1.284 GPa

@Temperature -50.0 °C
 186.2 ksi

@Temperature -58.0 °F
 Dynamic; ISO 11403-1 -2
Secant Modulus 0.396 GPa

@Strain 10.7 %,
Temperature 40.0 °C
 57.5 ksi

@Strain 10.7 %,
Temperature 104 °F
 ISO 11403-1 -2
0.481 GPa

@Strain 9.90 %,
Temperature 23.0 °C
 69.7 ksi

@Strain 9.90 %,
Temperature 73.4 °F
 ISO 11403-1 -2
0.709 GPa

@Strain 7.60 %,
Temperature 0.000 °C
 103 ksi

@Strain 7.60 %,
Temperature 32.0 °F
 ISO 11403-1 -2
0.750 GPa

@Strain 5.40 %,
Temperature 40.0 °C
 109 ksi

@Strain 5.40 %,
Temperature 104 °F
 ISO 11403-1 -2
0.793 GPa

@Strain 7.40 %,
Temperature -20.0 °C
 115 ksi

@Strain 7.40 %,
Temperature -4.00 °F
 ISO 11403-1 -2
0.912 GPa

@Strain 5.00 %,
Temperature 23.0 °C
 132 ksi

@Strain 5.00 %,
Temperature 73.4 °F
 ISO 11403-1 -2
1.32 GPa

@Strain 3.80 %,
Temperature 0.000 °C
 192 ksi

@Strain 3.80 %,
Temperature 32.0 °F
 ISO 11403-1 -2
1.48 GPa

@Strain 3.70 %,
Temperature -20.0 °C
 215 ksi

@Strain 3.70 %,
Temperature -4.00 °F
 ISO 11403-1 -2
1.94 GPa

@Strain 1.40 %,
Temperature 40.0 °C
 282 ksi

@Strain 1.40 %,
Temperature 104 °F
 ISO 11403-1 -2
2.63 GPa

@Strain 1.20 %,
Temperature 23.0 °C
 382 ksi

@Strain 1.20 %,
Temperature 73.4 °F
 ISO 11403-1 -2
3.05 GPa

@Strain 1.00 %,
Temperature 0.000 °C
 442 ksi

@Strain 1.00 %,
Temperature 32.0 °F
 ISO 11403-1 -2
3.56 GPa

@Strain 0.900 %,
Temperature -20.0 °C
 516 ksi

@Strain 0.900 %,
Temperature -4.00 °F
 ISO 11403-1 -2
Izod Impact, Notched (ISO) 3.00 kJ/m²
1.43 ft-lb/in²
ISO 180/1A
Charpy Impact Unnotched 4.00 J/cm²
19.0 ft-lb/in²
ISO 179/1eU
3.50 J/cm²

@Temperature -30.0 °C
 16.7 ft-lb/in²

@Temperature -22.0 °F
 ISO 179/1eU
Charpy Impact, Notched 0.300 J/cm²
1.43 ft-lb/in²
ISO 179/1eA
0.300 J/cm²

@Temperature -30.0 °C
 1.43 ft-lb/in²

@Temperature -22.0 °F
 ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 110 µm/m-°C
61.1 µin/in-°F
ISO 11359-1/-2
CTE, linear, Transverse to Flow 100 µm/m-°C
55.6 µin/in-°F
ISO 11359-1/-2
Melting Point 178 °C
352 °F
10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi) 160 °C
320 °F
ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 92.0 °C
198 °F
ISO 75-1/-2
Electrical Properties Metric English Comments
Surface Resistance >= 1.00e+15 ohm
>= 1.00e+15 ohm
IEC 60093
Comparative Tracking Index 600 V
600 V
IEC 60112