DuPont Performance Polymers Crastin® SK608 BK509 PBT  (Unverified Data**)

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 50% Glass Fiber Filled
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Crastin® SK608 BK509 PBT  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Crastin® SK608 BK509 is a 45% glass fiber reinforced, lubricated, black polybutylene terephthalate resin for injection molding.Information provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.66 g/cc
0.0600 lb/in³
ISO 1183
Filler Content 45 %
45 %
Water Absorption 0.10 %

@Temperature 23.0 °C
 0.10 %

@Temperature 73.4 °F
 Equilibrium 50%RH; ISO 62, Similar to
0.30 %

@Temperature 23.0 °C
 0.30 %

@Temperature 73.4 °F
 Saturation, immersed; ISO 62, Similar to
Linear Mold Shrinkage, Flow 0.0040 cm/cm
0.0040 in/in
Annealed; ISO 294-4
0.0030 cm/cm

@Thickness 2.00 mm
 0.0030 in/in

@Thickness 0.0787 in
 ISO 294-4
Linear Mold Shrinkage, Transverse 0.0145 cm/cm
0.0145 in/in
Annealed; ISO 294-4
0.013 cm/cm

@Thickness 2.00 mm
 0.013 in/in

@Thickness 0.0787 in
 ISO 294-4
Melt Index of Compound 5.0 g/10 min

@Load 5.00 kg,
Temperature 250 °C
 5.0 g/10 min

@Load 11.0 lb,
Temperature 482 °F
 cm3/10 min; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 140 MPa

@Temperature 23.0 °C
 20300 psi

@Temperature 73.4 °F
 ISO 527
Tensile Stress 12.68 MPa

@Strain 0.220 %,
Temperature 120 °C
 1839 psi

@Strain 0.220 %,
Temperature 248 °F
 ISO 527
16.6 MPa

@Strain 0.210 %,
Temperature 60.0 °C
 2410 psi

@Strain 0.210 %,
Temperature 140 °F
 ISO 527
18.7 MPa

@Strain 0.270 %,
Temperature 90.0 °C
 2710 psi

@Strain 0.270 %,
Temperature 194 °F
 ISO 527
20.51 MPa

@Strain 0.150 %,
Temperature 23.0 °C
 2975 psi

@Strain 0.150 %,
Temperature 73.4 °F
 ISO 527
21.01 MPa

@Strain 0.210 %,
Temperature 40.0 °C
 3047 psi

@Strain 0.210 %,
Temperature 104 °F
 ISO 527
24.92 MPa

@Strain 0.460 %,
Temperature 120 °C
 3614 psi

@Strain 0.460 %,
Temperature 248 °F
 ISO 527
27.39 MPa

@Strain 0.420 %,
Temperature 90.0 °C
 3973 psi

@Strain 0.420 %,
Temperature 194 °F
 ISO 527
32.48 MPa

@Strain 0.430 %,
Temperature 60.0 °C
 4711 psi

@Strain 0.430 %,
Temperature 140 °F
 ISO 527
32.8 MPa

@Strain 0.670 %,
Temperature 120 °C
 4760 psi

@Strain 0.670 %,
Temperature 248 °F
 ISO 527
32.99 MPa

@Strain 0.340 %,
Temperature 40.0 °C
 4785 psi

@Strain 0.340 %,
Temperature 104 °F
 ISO 527
37.95 MPa

@Strain 0.650 %,
Temperature 90.0 °C
 5504 psi

@Strain 0.650 %,
Temperature 194 °F
 ISO 527
39.43 MPa

@Strain 0.910 %,
Temperature 120 °C
 5719 psi

@Strain 0.910 %,
Temperature 248 °F
 ISO 527
41.48 MPa

@Strain 0.310 %,
Temperature 23.0 °C
 6016 psi

@Strain 0.310 %,
Temperature 73.4 °F
 ISO 527
43.65 MPa

@Strain 0.620 %,
Temperature 60.0 °C
 6331 psi

@Strain 0.620 %,
Temperature 140 °F
 ISO 527
43.69 MPa

@Strain 0.800 %,
Temperature 90.0 °C
 6337 psi

@Strain 0.800 %,
Temperature 194 °F
 ISO 527
43.98 MPa

@Strain 1.11 %,
Temperature 120 °C
 6379 psi

@Strain 1.11 %,
Temperature 248 °F
 ISO 527
45.53 MPa

@Strain 0.480 %,
Temperature 40.0 °C
 6604 psi

@Strain 0.480 %,
Temperature 104 °F
 ISO 527
48.16 MPa

@Strain 1.35 %,
Temperature 120 °C
 6985 psi

@Strain 1.35 %,
Temperature 248 °F
 ISO 527
50.75 MPa

@Strain 1.03 %,
Temperature 90.0 °C
 7361 psi

@Strain 1.03 %,
Temperature 194 °F
 ISO 527
51.12 MPa

@Strain 1.56 %,
Temperature 120 °C
 7414 psi

@Strain 1.56 %,
Temperature 248 °F
 ISO 527
52.9 MPa

@Strain 0.810 %,
Temperature 60.0 °C
 7670 psi

@Strain 0.810 %,
Temperature 140 °F
 ISO 527
53.5 MPa

@Strain 1.76 %,
Temperature 120 °C
 7760 psi

@Strain 1.76 %,
Temperature 248 °F
 ISO 527
55.63 MPa

@Strain 2.00 %,
Temperature 120 °C
 8068 psi

@Strain 2.00 %,
Temperature 248 °F
 ISO 527
56.21 MPa

@Strain 1.26 %,
Temperature 90.0 °C
 8153 psi

@Strain 1.26 %,
Temperature 194 °F
 ISO 527
56.33 MPa

@Strain 0.620 %,
Temperature 40.0 °C
 8170 psi

@Strain 0.620 %,
Temperature 104 °F
 ISO 527
57.0 MPa

@Strain 2.21 %,
Temperature 120 °C
 8270 psi

@Strain 2.21 %,
Temperature 248 °F
 ISO 527
57.4 MPa

@Strain 0.440 %,
Temperature 23.0 °C
 8330 psi

@Strain 0.440 %,
Temperature 73.4 °F
 ISO 527
59.23 MPa

@Strain 1.42 %,
Temperature 90.0 °C
 8591 psi

@Strain 1.42 %,
Temperature 194 °F
 ISO 527
61.94 MPa

@Strain 1.03 %,
Temperature 60.0 °C
 8984 psi

@Strain 1.03 %,
Temperature 140 °F
 ISO 527
62.93 MPa

@Strain 1.65 %,
Temperature 90.0 °C
 9127 psi

@Strain 1.65 %,
Temperature 194 °F
 ISO 527
65.6 MPa

@Strain 0.750 %,
Temperature 40.0 °C
 9510 psi

@Strain 0.750 %,
Temperature 104 °F
 ISO 527
65.85 MPa

@Strain 1.88 %,
Temperature 90.0 °C
 9551 psi

@Strain 1.88 %,
Temperature 194 °F
 ISO 527
67.39 MPa

@Strain 2.03 %,
Temperature 90.0 °C
 9774 psi

@Strain 2.03 %,
Temperature 194 °F
 ISO 527
68.28 MPa

@Strain 1.22 %,
Temperature 60.0 °C
 9903 psi

@Strain 1.22 %,
Temperature 140 °F
 ISO 527
71.91 MPa

@Strain 0.580 %,
Temperature 23.0 °C
 10430 psi

@Strain 0.580 %,
Temperature 73.4 °F
 ISO 527
73.54 MPa

@Strain 1.41 %,
Temperature 60.0 °C
 10670 psi

@Strain 1.41 %,
Temperature 140 °F
 ISO 527
73.79 MPa

@Strain 0.890 %,
Temperature 40.0 °C
 10700 psi

@Strain 0.890 %,
Temperature 104 °F
 ISO 527
78.59 MPa

@Strain 1.63 %,
Temperature 60.0 °C
 11400 psi

@Strain 1.63 %,
Temperature 140 °F
 ISO 527
80.4 MPa

@Strain 1.03 %,
Temperature 40.0 °C
 11700 psi

@Strain 1.03 %,
Temperature 104 °F
 ISO 527
82.14 MPa

@Strain 1.82 %,
Temperature 60.0 °C
 11910 psi

@Strain 1.82 %,
Temperature 140 °F
 ISO 527
84.7 MPa

@Strain 0.710 %,
Temperature 23.0 °C
 12300 psi

@Strain 0.710 %,
Temperature 73.4 °F
 ISO 527
85.03 MPa

@Strain 2.01 %,
Temperature 60.0 °C
 12330 psi

@Strain 2.01 %,
Temperature 140 °F
 ISO 527
86.07 MPa

@Strain 1.17 %,
Temperature 40.0 °C
 12480 psi

@Strain 1.17 %,
Temperature 104 °F
 ISO 527
91.43 MPa

@Strain 1.30 %,
Temperature 40.0 °C
 13260 psi

@Strain 1.30 %,
Temperature 104 °F
 ISO 527
98.64 MPa

@Strain 0.870 %,
Temperature 23.0 °C
 14310 psi

@Strain 0.870 %,
Temperature 73.4 °F
 ISO 527
100.4 MPa

@Strain 1.60 %,
Temperature 40.0 °C
 14560 psi

@Strain 1.60 %,
Temperature 104 °F
 ISO 527
108.1 MPa

@Strain 1.00 %,
Temperature 23.0 °C
 15680 psi

@Strain 1.00 %,
Temperature 73.4 °F
 ISO 527
116.2 MPa

@Strain 1.14 %,
Temperature 23.0 °C
 16850 psi

@Strain 1.14 %,
Temperature 73.4 °F
 ISO 527
123 MPa

@Strain 1.27 %,
Temperature 23.0 °C
 17800 psi

@Strain 1.27 %,
Temperature 73.4 °F
 ISO 527
129.8 MPa

@Strain 1.43 %,
Temperature 23.0 °C
 18830 psi

@Strain 1.43 %,
Temperature 73.4 °F
 ISO 527
Elongation at Break 2.0 %

@Temperature 23.0 °C
 2.0 %

@Temperature 73.4 °F
 ISO 527
Tensile Modulus 14.2 GPa

@Temperature 23.0 °C
 2060 ksi

@Temperature 73.4 °F
 ISO 527
Flexural Strength 210 MPa

@Temperature 23.0 °C
 30500 psi

@Temperature 73.4 °F
 ISO 178
Flexural Modulus 13.3 GPa

@Temperature 23.0 °C
 1930 ksi

@Temperature 73.4 °F
 ISO 178
Izod Impact, Notched (ISO) 10.0 kJ/m²

@Temperature -30.0 °C
 4.76 ft-lb/in²

@Temperature -22.0 °F
 ISO 180/1A
10.0 kJ/m²

@Temperature 23.0 °C
 4.76 ft-lb/in²

@Temperature 73.4 °F
 ISO 180/1A