DuPont Performance Polymers Crastin® HR5315HFS BK591 Polybutylene Terephthalate (PBT)  (Unverified Data**)

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 20% Glass Fiber Filled
Manufacturer DuPont Performance Polymers
Trade Name Crastin®
Port Shanghai port,China
Trade Terms EXW, FOB, CFR, CIF
Payment Terms L/C, T/T, PayPal
Download PDF DuPont Performance Polymers Crastin® HR5315HFS BK591 Polybutylene Terephthalate (PBT)  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
15% Glass Reinforced Hydrolysis Resistant Polybutylene Terephthalate with Improved Processing Crastin HR5315HFS is a 15% glass fiber reinforced moderatley toughened hydrolysis resistant polybutylene terephthalate for injection molding.Information provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.38 g/cc
0.0499 lb/in³
ISO 1183
Water Absorption 0.40 %
<br>@Thickness 2.00 mm
 0.40 %
<br>@Thickness 0.0787 in
 Sim. to ISO 62
Moisture Absorption 0.150 %
<br>@Thickness 2.00 mm
 0.150 %
<br>@Thickness 0.0787 in
 Sim. to ISO 62
Viscosity 175000 cP
<br>@Temperature 250 °C
 175000 cP
<br>@Temperature 482 °F
 @ 1000 sec-1; ISO 11443
Linear Mold Shrinkage, Flow 0.0050 cm/cm
0.0050 in/in
ISO 294-4 2577
Linear Mold Shrinkage, Transverse 0.011 cm/cm
0.011 in/in
ISO 294-4 2577
Melt Flow 13.5 g/10 min
<br>@Load 2.16 kg,<br> Temperature 250 °C
 13.5 g/10 min
<br>@Load 4.76 lb,<br> Temperature 482 °F
 cm³/10min; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 95.0 MPa
13800 psi
ISO 527-1/-2
Tensile Stress 3.53 MPa
<br>@Strain 0.200 %,<br> Temperature 150 °C
 512 psi
<br>@Strain 0.200 %,<br> Temperature 302 °F
 ISO 11403-1 -2
4.50 MPa
<br>@Strain 0.180 %,<br> Temperature 90.0 °C
 653 psi
<br>@Strain 0.180 %,<br> Temperature 194 °F
 ISO 11403-1 -2
9.81 MPa
<br>@Strain 0.250 %,<br> Temperature 40.0 °C
 1420 psi
<br>@Strain 0.250 %,<br> Temperature 104 °F
 ISO 11403-1 -2
17.03 MPa
<br>@Strain 0.280 %,<br> Temperature 0.000 °C
 2470 psi
<br>@Strain 0.280 %,<br> Temperature 32.0 °F
 ISO 11403-1 -2
18.3 MPa
<br>@Strain 1.47 %,<br> Temperature 150 °C
 2650 psi
<br>@Strain 1.47 %,<br> Temperature 302 °F
 ISO 11403-1 -2
19.02 MPa
<br>@Strain 0.350 %,<br> Temperature 23.0 °C
 2759 psi
<br>@Strain 0.350 %,<br> Temperature 73.4 °F
 ISO 11403-1 -2
23.6 MPa
<br>@Strain 0.350 %,<br> Temperature -40.0 °C
 3420 psi
<br>@Strain 0.350 %,<br> Temperature -40.0 °F
 ISO 11403-1 -2
23.63 MPa
<br>@Strain 1.18 %,<br> Temperature 90.0 °C
 3427 psi
<br>@Strain 1.18 %,<br> Temperature 194 °F
 ISO 11403-1 -2
27.2 MPa
<br>@Strain 3.06 %,<br> Temperature 150 °C
 3950 psi
<br>@Strain 3.06 %,<br> Temperature 302 °F
 ISO 11403-1 -2
32.14 MPa
<br>@Strain 4.77 %,<br> Temperature 150 °C
 4662 psi
<br>@Strain 4.77 %,<br> Temperature 302 °F
 ISO 11403-1 -2
37.94 MPa
<br>@Strain 2.48 %,<br> Temperature 90.0 °C
 5503 psi
<br>@Strain 2.48 %,<br> Temperature 194 °F
 ISO 11403-1 -2
38.76 MPa
<br>@Strain 1.14 %,<br> Temperature 40.0 °C
 5622 psi
<br>@Strain 1.14 %,<br> Temperature 104 °F
 ISO 11403-1 -2
45.25 MPa
<br>@Strain 3.90 %,<br> Temperature 90.0 °C
 6563 psi
<br>@Strain 3.90 %,<br> Temperature 194 °F
 ISO 11403-1 -2
46.09 MPa
<br>@Strain 0.790 %,<br> Temperature -20.0 °C
 6685 psi
<br>@Strain 0.790 %,<br> Temperature -4.00 °F
 ISO 11403-1 -2
50.49 MPa
<br>@Strain 0.890 %,<br> Temperature 0.000 °C
 7323 psi
<br>@Strain 0.890 %,<br> Temperature 32.0 °F
 ISO 11403-1 -2
51.42 MPa
<br>@Strain 1.02 %,<br> Temperature 23.0 °C
 7458 psi
<br>@Strain 1.02 %,<br> Temperature 73.4 °F
 ISO 11403-1 -2
56.18 MPa
<br>@Strain 1.97 %,<br> Temperature 40.0 °C
 8148 psi
<br>@Strain 1.97 %,<br> Temperature 104 °F
 ISO 11403-1 -2
63.58 MPa
<br>@Strain 1.03 %,<br> Temperature -40.0 °C
 9222 psi
<br>@Strain 1.03 %,<br> Temperature -40.0 °F
 ISO 11403-1 -2
67.81 MPa
<br>@Strain 2.86 %,<br> Temperature 40.0 °C
 9835 psi
<br>@Strain 2.86 %,<br> Temperature 104 °F
 ISO 11403-1 -2
71.17 MPa
<br>@Strain 1.33 %,<br> Temperature 0.000 °C
 10320 psi
<br>@Strain 1.33 %,<br> Temperature 32.0 °F
 ISO 11403-1 -2
73.66 MPa
<br>@Strain 1.64 %,<br> Temperature 23.0 °C
 10680 psi
<br>@Strain 1.64 %,<br> Temperature 73.4 °F
 ISO 11403-1 -2
77.15 MPa
<br>@Strain 1.40 %,<br> Temperature -20.0 °C
 11190 psi
<br>@Strain 1.40 %,<br> Temperature -4.00 °F
 ISO 11403-1 -2
87.37 MPa
<br>@Strain 2.28 %,<br> Temperature 23.0 °C
 12670 psi
<br>@Strain 2.28 %,<br> Temperature 73.4 °F
 ISO 11403-1 -2
90.3 MPa
<br>@Strain 1.87 %,<br> Temperature 0.000 °C
 13100 psi
<br>@Strain 1.87 %,<br> Temperature 32.0 °F
 ISO 11403-1 -2
90.59 MPa
<br>@Strain 1.56 %,<br> Temperature -40.0 °C
 13140 psi
<br>@Strain 1.56 %,<br> Temperature -40.0 °F
 ISO 11403-1 -2
99.89 MPa
<br>@Strain 1.98 %,<br> Temperature -20.0 °C
 14490 psi
<br>@Strain 1.98 %,<br> Temperature -4.00 °F
 ISO 11403-1 -2
112.87 MPa
<br>@Strain 2.10 %,<br> Temperature -40.0 °C
 16370 psi
<br>@Strain 2.10 %,<br> Temperature -40.0 °F
 ISO 11403-1 -2
119.15 MPa
<br>@Strain 2.71 %,<br> Temperature -20.0 °C
 17281 psi
<br>@Strain 2.71 %,<br> Temperature -4.00 °F
 ISO 11403-1 -2
Elongation at Break 3.3 %
3.3 %
ISO 527-1/-2
Tensile Modulus 5.00 GPa
725 ksi
ISO 527-1/-2
Flexural Strength 143 MPa
20700 psi
ISO 178
Secant Modulus 2.00 GPa
<br>@Strain 3.60 %,<br> Temperature 40.0 °C
 290 ksi
<br>@Strain 3.60 %,<br> Temperature 104 °F
 ISO 11403-1 -2
2.70 GPa
<br>@Strain 2.24 %,<br> Temperature 40.0 °C
 392 ksi
<br>@Strain 2.24 %,<br> Temperature 104 °F
 ISO 11403-1 -2
3.38 GPa
<br>@Strain 2.76 %,<br> Temperature 23.0 °C
 491 ksi
<br>@Strain 2.76 %,<br> Temperature 73.4 °F
 ISO 11403-1 -2
3.40 GPa
<br>@Strain 1.14 %,<br> Temperature 40.0 °C
 493 ksi
<br>@Strain 1.14 %,<br> Temperature 104 °F
 ISO 11403-1 -2
3.87 GPa
<br>@Strain 3.30 %,<br> Temperature -20.0 °C
 562 ksi
<br>@Strain 3.30 %,<br> Temperature -4.00 °F
 ISO 11403-1 -2
3.924 GPa
<br>@Strain 0.250 %,<br> Temperature 40.0 °C
 569.1 ksi
<br>@Strain 0.250 %,<br> Temperature 104 °F
 ISO 11403-1 -2
4.28 GPa
<br>@Strain 1.85 %,<br> Temperature 23.0 °C
 621 ksi
<br>@Strain 1.85 %,<br> Temperature 73.4 °F
 ISO 11403-1 -2
4.38 GPa
<br>@Strain 2.31 %,<br> Temperature 0.000 °C
 635 ksi
<br>@Strain 2.31 %,<br> Temperature 32.0 °F
 ISO 11403-1 -2
4.86 GPa
<br>@Strain 2.20 %,<br> Temperature -20.0 °C
 705 ksi
<br>@Strain 2.20 %,<br> Temperature -4.00 °F
 ISO 11403-1 -2
5.04 GPa
<br>@Strain 1.02 %,<br> Temperature 23.0 °C
 731 ksi
<br>@Strain 1.02 %,<br> Temperature 73.4 °F
 ISO 11403-1 -2
5.09 GPa
<br>@Strain 2.49 %,<br> Temperature -40.0 °C
 738 ksi
<br>@Strain 2.49 %,<br> Temperature -40.0 °F
 ISO 11403-1 -2
5.22 GPa
<br>@Strain 1.49 %,<br> Temperature 0.000 °C
 756 ksi
<br>@Strain 1.49 %,<br> Temperature 32.0 °F
 ISO 11403-1 -2
5.43 GPa
<br>@Strain 0.350 %,<br> Temperature 23.0 °C
 788 ksi
<br>@Strain 0.350 %,<br> Temperature 73.4 °F
 ISO 11403-1 -2
5.51 GPa
<br>@Strain 1.40 %,<br> Temperature -20.0 °C
 799 ksi
<br>@Strain 1.40 %,<br> Temperature -4.00 °F
 ISO 11403-1 -2
5.67 GPa
<br>@Strain 0.890 %,<br> Temperature 0.000 °C
 823 ksi
<br>@Strain 0.890 %,<br> Temperature 32.0 °F
 ISO 11403-1 -2
5.68 GPa
<br>@Strain 1.73 %,<br> Temperature -40.0 °C
 824 ksi
<br>@Strain 1.73 %,<br> Temperature -40.0 °F
 ISO 11403-1 -2
5.83 GPa
<br>@Strain 0.790 %,<br> Temperature -20.0 °C
 846 ksi
<br>@Strain 0.790 %,<br> Temperature -4.00 °F
 ISO 11403-1 -2
6.08 GPa
<br>@Strain 0.280 %,<br> Temperature 0.000 °C
 882 ksi
<br>@Strain 0.280 %,<br> Temperature 32.0 °F
 ISO 11403-1 -2
6.17 GPa
<br>@Strain 1.03 %,<br> Temperature -40.0 °C
 895 ksi
<br>@Strain 1.03 %,<br> Temperature -40.0 °F
 ISO 11403-1 -2
6.74 GPa
<br>@Strain 0.350 %,<br> Temperature -40.0 °C
 978 ksi
<br>@Strain 0.350 %,<br> Temperature -40.0 °F
 ISO 11403-1 -2
Charpy Impact Unnotched 5.70 J/cm²
27.1 ft-lb/in²
ISO 179/1eU
Charpy Impact, Notched 1.10 J/cm²
5.23 ft-lb/in²
ISO 179/1eA
0.600 J/cm²
<br>@Temperature -30.0 °C
 2.86 ft-lb/in²
<br>@Temperature -22.0 °F
 ISO 179/1eA
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+15 ohm-cm
>= 1.00e+15 ohm-cm
IEC 60093
Surface Resistance >= 1.00e+15 ohm
>= 1.00e+15 ohm
IEC 60093
Dielectric Strength 35.0 kV/mm
889 kV/in
IEC 60243-1
Dissipation Factor 0.010
<br>@Frequency 100 Hz
 0.010
<br>@Frequency 100 Hz
 IEC 60250